Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PPA UCL-4536 HS SABIC INNOVATIVE US

LNP™ LUBRICOMP™

Automotive components,Electronic and electrical accessories

Thermal stability,Flame retardant,Filler: Carbon fiber rein,30% filler by weight

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/UCL-4536 HS
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	259 °C
		0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	280 °C
		1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	260 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	278 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/UCL-4536 HS
Bending modulus	50.0mmSpan	ASTM D790	22400 Mpa
Bending modulus			ISO 178	22200 Mpa
bending strength		ISO 178	321 Mpa
bending strength		Break,50.0mmSpan	ASTM D790	326 Mpa
elongation	Break	ASTM D638	1.3 %
Friction coefficient	Dynamic	ASTM D3702Modified	0.35
Friction coefficient		Static	ASTM D3702Modified	0.32
Tensile modulus		ASTM D638	26400 Mpa
Tensile modulus			ISO 527-2/1	26100 Mpa
Tensile strain	Break	ISO 527-2/5	1.2 %
tensile strength	Break	ISO 527-2/5	229 Mpa
tensile strength		Break	ASTM D638	235 Mpa
Wear factor	Ring	ASTM D3702Modified	0.550 10^-10in^5-min/ft-lb-hr
Wear factor		Washer	ASTM D3702Modified	14.0 10^-10in^5-min/ft-lb-hr

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/UCL-4536 HS
Shrinkage rate	TD：24hr	ASTM D955	0.72 %
Shrinkage rate		MD：24hr	ASTM D955	0.11 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.40 %
Water absorption rate		24hr,50%RH	ASTM D570	0.26 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/UCL-4536 HS
Dart impact	23°C,TotalEnergy	ASTM D3763	5.60 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.2 kJ/m²
Multi axis Instrumented Impact Energy		ISO 6603-2	1.92 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	36 kJ/m²