COC TOPAS® 8007F-04 JAPAN POLYPLASTIC

294

Unit Price:US$ 13,517 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Dimensional stability｜Chemical resistance
Application Areas:LCD application｜Optical applications
Color:--
Grade:Optical grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Transmittance rate	2000μm	ISO 13468-2	91 %
Refractive index		ISO 489	1.53 °C
turbidity		ISO 13468-2	<=0.1 %
gloss		ISO 2813	>=100 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	MD,23°C	ISO 527-2	2200 Mpa
	Tensile modulus	Break拉伸强度	ISO 527-3	57 Mpa
		Tensile modulus	Break拉伸强度	ISO 527-3	50 Mpa
		Tensile modulus	Tensile modulus	Elmendorf撕裂强度	ISO 6383-2	225 g
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	20 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	2.6 kJ/m²
Tensile modulus	23°C	ISO 527-2	2600 Mpa
Elongation at Break	23°C	ISO 527-2	4.5 %
tensile strength	23°C	ISO 527-2	63 Mpa
Tensile modulus	TD,23°C	ISO 527-2	1800 Mpa
Elongation at Break	TD,23°C	ISO 527-2	3 %
Elongation at Break	Elongation at Break	MD,23°C	ISO 527-2	2.9 %
Tensile modulus	Elmendorf撕裂强度	ISO 6383-2	230 g
Tensile modulus	Tensile modulus	跌落试验	ISO 7765-1	<=36 g

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ISO 306/B50	80 °C
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	75 °C
Vicat softening temperature	玻璃转化温度	ISO 11357-2	78 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	厚度		70 microns
	melt mass-flow rate	水蒸气穿透率	ISO 15106-3	0.0008 g/m²/day
		melt mass-flow rate	氧渗透		997 cm3mil/(m2dayatm
		melt mass-flow rate	melt mass-flow rate	水蒸气渗透性		3.70 gmil/(m2day
Water absorption rate	(23°C,24hr)	ISO 62	0.01 %
melt mass-flow rate	260℃/2.16Kg	ISO 1133	32 cm3/10min
	melt mass-flow rate	230℃/2.16Kg	ISO 1133	11 g/10min
	melt mass-flow rate	melt mass-flow rate	190℃/2.16Kg	ISO 1133	1.8 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	相对漏电起痕指数	IEC 60112	600 V
Dielectric constant	23°C	IEC 60250	2.35 1kHz
Volume resistivity		IEC 60093	1E+14 Ω.cm

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 1.50mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

COC TOPAS® 8007F-04 JAPAN POLYPLASTIC

Material Description

Technical Data Sheet Compare

Technical Data Sheet