Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 8007F-04 JAPAN POLYPLASTIC
TOPAS®
LCD application、Optical applications
Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-04 |
|---|---|---|---|
| Tensile modulus | MD,23°C | ISO 527-2 | 2200 Mpa |
| 跌落试验 | ISO 7765-1 | <=36 g | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.6 kJ/m² |
| elongation at break | TD,23°C | ISO 527-2 | 3 % |
| Tensile modulus | 断裂拉伸强度 | ISO 527-3 | 50 Mpa |
| 23°C | ISO 527-2 | 2600 Mpa | |
| elongation at break | MD,23°C | ISO 527-2 | 2.9 % |
| Tensile modulus | TD,23°C | ISO 527-2 | 1800 Mpa |
| Elmendorf撕裂强度 | ISO 6383-2 | 230 g | |
| elongation at break | 23°C | ISO 527-2 | 4.5 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 20 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 63 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-04 |
|---|---|---|---|
| dielectric constant | 23°C | IEC 60250 | 2.35 1kHz |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm |
| optical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-04 |
|---|---|---|---|
| gloss | ISO 2813 | >=100 % | |
| refractive index | ISO 489 | 1.53 °C | |
| transmittance | 2000μm | ISO 13468-2 | 91 % |
| Haze ratio | ISO 13468-2 | <=0.1 % |
| Flame retardant performance | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-04 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-04 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.01 % |
| melt mass-flow rate | 230℃/2.16Kg | ISO 1133 | 11 g/10min |
| 260℃/2.16Kg | ISO 1133 | 32 cm3/10min | |
| 水蒸气渗透性 | 3.70 gmil/(m2day | ||
| 水蒸气穿透率 | ISO 15106-3 | 0.0008 g/m²/day | |
| 厚度 | 70 microns | ||
| 190℃/2.16Kg | ISO 1133 | 1.8 g/10min | |
| 氧渗透 | 997 cm3mil/(m2dayatm |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-04 |
|---|---|---|---|
| vicat | ISO 306/B50 | 80 °C | |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 75 °C |
| vicat | 玻璃转化温度 | ISO 11357-2 | 78 °C |