PBT/PET VALOX™  8032UX SABIC INNOVATIVE US

323
  • Unit Price:US$ 3,276 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:enhance｜Filler: Glass fiber reinforced material｜30%｜Filler by weight
  • Application Areas:chip｜Shell｜Home appliance components｜Phone case
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 179/1eU45 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU40 kJ/m²
-30°CASTM D25648 J/m
23°CASTM D25657 J/m
-30°CISO 180/1A8.0 kJ/m²
0°CISO 180/1A8.0 kJ/m²
23°CISO 180/1A9.0 kJ/m²
-30°CASTM D4812470 J/m
23°CASTM D4812480 J/m
-30°CISO 180/1U40 kJ/m²
23°CISO 180/1U45 kJ/m²
Dart impact23°C,TotalEnergyASTM D37638.00 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.60mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
--3ASTM D6389950 Mpa
yieldASTM D638115 Mpa
yieldISO 527-2/5145 Mpa
crackASTM D638115 Mpa
crackISO 527-2/5145 Mpa
yieldASTM D6382.0 %
yieldISO 527-2/52.4 %
crackASTM D6382.0 %
crackISO 527-2/52.5 %
50.0mm spanASTM D7908450 Mpa
--9ISO 1788500 Mpa
--10ISO 178210 Mpa
Yield, 50.0mm spanASTM D790165 Mpa
Taber abraser1000Cycles,1000g,CS-17WheelInternal Method30.0 mg
thermal performanceTest ConditionTest MethodTest Result
Flow: 23 to 60 ° C23to60℃ISO 11359-22.2E-05 cm/cm/°C
Horizontal: -40 to 40 ° CAcross Flow, -40to40℃ASTME8317.5E-05 cm/cm/°C
Horizontal: 23 to 60 ° CAcross Flow, 23to60℃ISO 11359-28.1E-05 cm/cm/°C
0.45MPa, unannealed, 3.20mmASTM D648208 °C
0.45MPa, unannealed, 100mm spanISO 75-2/Be217 °C
1.8MPa, unannealed, 3.20mmASTM D648190 °C
1.8MPa, unannealed, 100mm spanISO 75-2/Ae195 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Flow: -40 to 40 ° CASTME8312.5E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate265°C/2.16kgASTM D123815 g/10min
Melt Volume Flow Rate (MVR)265°C/2.16kgISO 113315.0 cm3/10min
Shrinkage rateMD1Internal Method0.40-0.80 %
Shrinkage rateMD:3.20mmInternal Method0.40-0.80 %
Shrinkage rateTD2Internal Method0.60-1.0 %
Shrinkage rateTD:3.20mmInternal Method0.60-1.0 %
Water absorption rateSaturation,23°CISO 620.16 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.050 %
Electrical performanceTest ConditionTest MethodTest Result
Relative permittivity100HzIEC 602503.60
Relative permittivity1MHzIEC 602503.20
Dissipation factor50HzIEC 602508E-04
Dissipation factor60HzIEC 602508E-04
Dissipation factor1MHzIEC 602500.013
Compared to the anti leakage trace indexCTIUL 746PLC 2
Compared to the anti leakage trace indexIEC 60112PLC 2
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dielectric strength0.800mm,in OilIEC 60243-127 KV/mm
Dielectric strength1.60mm,in OilIEC 60243-123 KV/mm
Dielectric strength3.20mm,in OilIEC 60243-115 KV/mm
Relative permittivity50HzIEC 602503.30
Relative permittivity60HzIEC 602503.30
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-SaleISO 2039-2119
Ball Pressure TestH358/30ISO 2039-1110 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.