PBT NOVADURAN™ 5820G30 M MITSUBISHI ENGINEERING JAPAN
208
- Unit Price:US$ 4,269 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high strength
- Application Areas:Electronic and Electrical Applications｜Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 退火 | ISO 75-2/B | 212 °C |
| 1.8 MPa, 退火 | ISO 75-2/A | 178 °C | |
| melting temperature | ISO 11357-3 | 224 °C | |
| Linear coefficient of thermal expansion | 流动 : -30 到 35°C | ISO 11359-2 | 2.0E-5 cm/cm/°C |
| 流动 : -30 到 120°C | ISO 11359-2 | 2.0E-5 cm/cm/°C | |
| 流动 : 35 到 120°C | ISO 11359-2 | 2.0E-5 cm/cm/°C | |
| 横向 : -30 到 35°C | ISO 11359-2 | 8.0E-5 cm/cm/°C | |
| 横向 : -30 到 120°C | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| 横向 : 35 到 120°C | ISO 11359-2 | 1.4E-4 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 38 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 250°C/5.0 kg | ISO 1133 | 24.0 cm3/10min |
| shrinkage rate | 横向流量 : 2.00 mm | 内部方法 | 0.70 % |
| 流量 : 2.00 mm | 内部方法 | 0.30 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.070 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 6.0E+15 ohms | |
| volume resistivity | IEC 60093 | 1.0E+14 ohms·cm | |
| dielectric strength | 1.00 mm | IEC 60243-1 | 33 KV/mm |
| 2.00 mm | IEC 60243-1 | 30 KV/mm | |
| dielectric constant | 1 MHz | IEC 60250 | 3.30 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.017 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature - Vacuum Drying Machine | 120 °C | ||
| Drying time - vacuum dryer | 5.0 to 8.0 hr | ||
| Temperature at the rear of the barrel | 240 °C | ||
| Temperature in the middle of the barrel | 245 °C | ||
| Temperature at the front of the material cylinder | 255 °C | ||
| Spray nozzle temperature | 255 °C | ||
| mold temperature | 80 to 100 °C | ||
| Injection Pressure | 20.0 to 150 Mpa | ||
| injection speed | 中等偏快 | ||
| screw speed | 80 to 120 rpm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 10600 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 134 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| flexural modulus | ISO 178 | 9900 Mpa | |
| bending strength | ISO 178 | 190 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.