Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5820G30 M MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Electronic and Electrical Applications,Automotive sector
high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5820G30 M |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 38 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5820G30 M |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 10600 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 134 Mpa |
| bending strength | ISO 178 | 190 Mpa | |
| Flexural modulus | ISO 178 | 9900 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5820G30 M |
|---|---|---|---|
| dielectric strength | 2.00 mm | IEC 60243-1 | 30 KV/mm |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.017 |
| Volume resistivity | IEC 60093 | 1.0E+14 ohms·cm | |
| Surface Resistivity | IEC 60093 | 6.0E+15 ohms | |
| dielectric strength | 1.00 mm | IEC 60243-1 | 33 KV/mm |
| dielectric constant | 1 MHz | IEC 60250 | 3.30 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5820G30 M |
|---|---|---|---|
| Shrinkage rate | 横向流量 : 2.00 mm | 内部方法 | 0.70 % |
| Melt volume flow rate | 250°C/5.0 kg | ISO 1133 | 24.0 cm3/10min |
| Shrinkage rate | 流量 : 2.00 mm | 内部方法 | 0.30 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.070 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5820G30 M |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 224 °C | |
| Linear coefficient of thermal expansion | 流动 : -30 到 35°C | ISO 11359-2 | 2.0E-5 cm/cm/°C |
| 横向 : 35 到 120°C | ISO 11359-2 | 1.4E-4 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 退火，HDT | ISO 75-2/B | 212 °C |
| Linear coefficient of thermal expansion | 流动 : 35 到 120°C | ISO 11359-2 | 2.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 退火，HDT | ISO 75-2/A | 178 °C |
| Linear coefficient of thermal expansion | 横向 : -30 到 120°C | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| 横向 : -30 到 35°C | ISO 11359-2 | 8.0E-5 cm/cm/°C | |
| 流动 : -30 到 120°C | ISO 11359-2 | 2.0E-5 cm/cm/°C |
| injection | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5820G30 M |
|---|---|---|---|
| screw speed | 80 to 120 rpm | ||
| Temperature in the middle of the barrel | 245 °C | ||
| Temperature at the rear of the barrel | 240 °C | ||
| Injection Pressure | 20.0 to 150 Mpa | ||
| Drying Temperature - Vacuum Drying Machine | 120 °C | ||
| Temperature at the front of the material cylinder | 255 °C | ||
| Drying time - vacuum dryer | 5.0 to 8.0 hr | ||
| Temperature | 80 to 100 °C | ||
| injection speed | 中等偏快 | ||
| Spray nozzle temperature | 255 °C |