PA6

PA6 Amilan® CM1001G-15 TORAY JAPAN

370

Unit Price:US$ 2,432 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
177MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	kJ/m²	30
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-40°C	kJ/m²	20 25

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm		HB --

mechanical properties	Test Condition	Test Method	Test Result
Friction coefficient vs. Metal			0.15 --
Taber abraser	1000Cycles	mg	0.300 --
shear strength	23°C	MPa	100 --
Compressive stress	80°C	MPa	70.0 35.0
	Compressive stress	23°C	MPa	135 65.0
	Compressive stress	Compressive stress	-40°C	MPa	205 130
bending strength	80°C	MPa	80.0 45.0
	bending strength	23°C	MPa	170 85.0
	bending strength	bending strength	-40°C	MPa	205 --
Bending modulus	80°C	MPa	2300 1700
Bending modulus	Bending modulus	23°C	MPa	5700 2700
tensile strength	-40°C	MPa	135 115
	tensile strength	23°C	MPa	110 55.0
	tensile strength	tensile strength	80°C	MPa	45.0 25.0
Tensile strain	Break,-40°C	%	2.0 3.0
	Tensile strain	Break,23°C	%	2.0
	Tensile strain	Tensile strain	Break,80°C	%	5.5 6.0
Bending modulus	-40°C	MPa	7300 6000
Rockwell hardness		ASTM D785	R119.M90

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		W/m/K	0.31 --
specific heat		J/kg/°C	1700 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	4.5E-05 --
Melting temperature		°C	225 --
Hot deformation temperature	0.45MPa,Unannealed	°C	210 --
Melting temperature			225 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	%	8.3 --
Water absorption rate	Water absorption rate	23°C,24hr	%	1.3 --
Shrinkage rate	TD3：3.00mm	%	0.70-1.1 --
density		ASTM D792/ISO 1183	1.25
Water absorption rate		ASTM D570/ISO 62	1.3 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	23°C,1kHz		4.30 --
Dielectric constant	Dielectric constant	23°C,1MHz		3.70 --
Dissipation factor	23°C,50Hz		0.050 --
Dissipation factor	Dissipation factor	23°C,1kHz		0.040 --
Dielectric constant	23°C,50Hz		4.50 --
Dielectric strength		kV/mm	20 --
Volume resistivity		ohms·cm	1E+15 1E+12
Dissipation factor	23°C,1MHz		0.030 --
Arc resistance		sec	120 --
Volume resistivity		ASTM D257/IEC 60093	10^13 Ω.cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale,23°C		90 --
	Rockwell hardness	R-Sale,80°C		10 --
	Rockwell hardness	Rockwell hardness	R-Sale,23°C		119 --

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Amilan® CM1001G-15 TORAY JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet