Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1001G-15 TORAY JAPAN
Amilan®
--
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM1001G-15 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 20 25 |
| 23°C | kJ/m² | 30 |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM1001G-15 |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | 90 -- | |
| R计秤,23°C | 119 -- | ||
| R计秤,80°C | 10 -- |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM1001G-15 |
|---|---|---|---|
| tensile strength | 23°C | MPa | 110 55.0 |
| Flexural modulus | 23°C | MPa | 5700 2700 |
| Taber abraser | 1000Cycles | mg | 0.300 -- |
| tensile strength | -40°C | MPa | 135 115 |
| compression stress | 23°C | MPa | 135 65.0 |
| Flexural modulus | 80°C | MPa | 2300 1700 |
| bending strength | 80°C | MPa | 80.0 45.0 |
| shear strength | 23°C | MPa | 100 -- |
| tensile strength | 80°C | MPa | 45.0 25.0 |
| Rockwell hardness | ASTM D785 | R119.M90 | |
| compression stress | -40°C | MPa | 205 130 |
| bending strength | 23°C | MPa | 170 85.0 |
| Tensile strain | 断裂,23°C | % | 2.0 |
| 断裂,80°C | % | 5.5 6.0 | |
| Flexural modulus | -40°C | MPa | 7300 6000 |
| bending strength | -40°C | MPa | 205 -- |
| Tensile strain | 断裂,-40°C | % | 2.0 3.0 |
| compression stress | 80°C | MPa | 70.0 35.0 |
| Friction coefficient - vs. Metal | 0.15 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM1001G-15 |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | 4.50 -- | |
| 23°C,1MHz | 3.70 -- | ||
| arc resistance | sec | 120 -- | |
| Dissipation Factor | 23°C,50Hz | 0.050 -- | |
| 23°C,1MHz | 0.030 -- | ||
| dielectric constant | 23°C,1kHz | 4.30 -- | |
| Volume resistivity | ohms·cm | 1E+15 1E+12 | |
| dielectric strength | kV/mm | 20 -- | |
| Dissipation Factor | 23°C,1kHz | 0.040 -- | |
| Volume resistivity | ASTM D257/IEC 60093 | 10^13 Ω.cm |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM1001G-15 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.25 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.3 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM1001G-15 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | HB -- |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM1001G-15 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | % | 8.3 -- |
| Shrinkage rate | TD3：3.00mm | % | 0.70-1.1 -- |
| Water absorption rate | 23°C,24hr | % | 1.3 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM1001G-15 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 210 -- |
| melting temperature | °C | 225 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 4.5E-05 -- |
| specific heat | J/kg/°C | 1700 -- | |
| thermal conductivity | W/m/K | 0.31 -- | |
| melting temperature | 225 ℃（℉） |