PBT

PBT Cristin® ST820 NC010 DUPONT USA

250

Unit Price:US$ 6,122 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
82MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance
Application Areas:Electronic and electrical components
Color:--
Grade:Toughened grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			无筋.超级坚固.注射成型

Other performance	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ASTM D2863	22 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	-40°C	ISO 180/1U	270 kJ/m²
	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	ISO 3795	38 mm/min
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	19 %
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	1E-04 g

mechanical properties	Test Condition	Test Method	Test Result
Elongation at Break		ASTM D638/ISO 527	150 %
Tensile modulus		ASTM D638/ISO 527	1700 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	1550 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	50 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ISO 527-2	1700 Mpa
tensile strength	Yield	ISO 527-2	38.0 Mpa
Tensile strain	Yield	ISO 527-2	7.0 %
Nominal tensile fracture strain		ISO 527-2	>50 %
Bending modulus		ISO 178	1550 Mpa
bending strength		ISO 178	50.0 Mpa
compressive strength	23℃	ASTM D695	43 MPa
tensile strength	23℃	ASTM D638	37 MPa
Tensile modulus	23℃	ASTM D638	1600 MPa
Bending modulus	23℃	ASTM D790	1680 MPa
bending strength	23℃	ASTM D638	53 MPa
Elongation at Break	23℃	ASTM D638	150 %
Impact strength of cantilever beam gap		ASTM D256	117 J/m
	Impact strength of cantilever beam gap	-40℃	ASTM D256	117 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃	ASTM D256	No Break J/m
Suspended wall beam without notch impact strength	-40℃	ASTM D256	No Break J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23℃	ASTM D256	No Break J/m

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	HB(0.8mm)
Hot deformation temperature	HDT	ASTM D648/ISO 75	100 ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	145 ℃（℉）
Melting temperature			225 ℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	216 ℃（℉）
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	100 °C
	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	145 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	50.0 °C
Vicat softening temperature		ISO 306/B50	125 °C
Melting temperature		ISO 11357-3	225 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.9E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.9E-04 cm/cm/°C
Melting temperature		℃	225 225
Hot deformation temperature	264 psi，Unannealed	ASTM D648	47 ℃
Linear coefficient of thermal expansion	平行Flow	ASTM E831	0.00019 cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	垂直Flow	ASTM E831	0.00019 cm/cm/℃

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1220
Shrinkage rate		ASTM D955	1.8 %
Water absorption rate		ASTM D570/ISO 62	0.12 %
Shrinkage rate	TD	ISO 294-4	1.8 %
Shrinkage rate	Shrinkage rate	MD2	ISO 294-4	2.5 %
MediumDensity			1.03 g/cm³
Top out temperature			170 °C
SpecificHeatCapacity of Melt			2100 J/kg/°C
ThermalConductivityofMelt			0.20 W/m/K
Shrinkage rate	MD	ISO 294-4	1.9 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.31 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.12 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257/IEC 60093	1.00E+15 Ω
Volume resistivity		ASTM D257/IEC 60093	>1E13 Ω.cm
Dielectric strength		IEC 60243-1	27 KV/mm
Dissipation factor	100Hz	IEC 60250	0.020
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.019
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		IEC 60093	1E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ISO 2039-2	104

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Cristin® ST820 NC010 DUPONT USA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet