PA6 Ultramid® 8233G MT7499 BASF GERMANY

165

Unit Price:US$ 1,837 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜high strength｜Oil resistant
Application Areas:Helmet｜Automotive Applications｜Engine parts
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.39 g/cm³
density	density		ISO 1183	1.39 g/cm³
Shrinkage rate			0.30 %
Water absorption rate		ASTM D570	1.1 %
	Water absorption rate		ISO 62	1.1 %
		Water absorption rate		ASTM D570	6.4 %
			Water absorption rate		ISO 62	6.4 %
				Water absorption rate		ASTM D570	1.8 %
				Water absorption rate	Water absorption rate		ISO 62	1.8 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	121

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
	UL flame retardant rating		UL 94	HB
		UL flame retardant rating		UL 94	HB
		UL flame retardant rating	UL flame retardant rating		UL 94	HB

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO 180	8.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	10 kJ/m²
Dart impact		内部方法	4.07 J
Charpy Notched Impact Strength		ISO 179	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179	15 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	88 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	110 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	150 J/m

Mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790	297 Mpa
	bending strength		ASTM D790	160 Mpa
		bending strength		ASTM D790	140 Mpa
			bending strength		ASTM D790	112 Mpa
			bending strength	bending strength		ISO 178	260 Mpa
Tensile modulus		ISO 527-2	10500 Mpa
	Tensile modulus		ISO 527-2	10100 Mpa
		Tensile modulus		ISO 527-2	4430 Mpa
			Tensile modulus		ISO 527-2	3550 Mpa
			Tensile modulus	Tensile modulus		ISO 527-2	3440 Mpa
tensile strength		ASTM D638	283 Mpa
	tensile strength		ASTM D638	195 Mpa
		tensile strength		ASTM D638	110 Mpa
			tensile strength		ASTM D638	83.0 Mpa
				tensile strength		ISO 527-2	283 Mpa
					tensile strength		ISO 527-2	185 Mpa
						tensile strength		ISO 527-2	110 Mpa
							tensile strength		ISO 527-2	83.0 Mpa
							tensile strength	tensile strength		ISO 527-2	80.0 Mpa
elongation		ASTM D638	3.6 %
	elongation		ASTM D638	3.5 %
		elongation		ASTM D638	7.0 %
		elongation	elongation		ASTM D638	7.0 %
Tensile strain		ISO 527-2	3.6 %
	Tensile strain		ISO 527-2	3.5 %
		Tensile strain		ISO 527-2	7.0 %
			Tensile strain		ISO 527-2	7.0 %
			Tensile strain	Tensile strain		ISO 527-2	6.0 %
Flexural modulus		ASTM D790	9830 Mpa
	Flexural modulus		ASTM D790	9040 Mpa
		Flexural modulus		ASTM D790	4020 Mpa
			Flexural modulus		ASTM D790	3750 Mpa
				Flexural modulus		ASTM D790	3320 Mpa
				Flexural modulus	Flexural modulus		ISO 178	8200 Mpa
bending strength		ASTM D790	380 Mpa

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	>1.0E+13 ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	>1.0E+13 ohms·cm
dielectric strength		IEC 60243-1	44 KV/mm
dielectric constant		IEC 60250	4.20
dielectric constant	dielectric constant		IEC 60250	3.60
Dissipation Factor		IEC 60250	0.020
Dissipation Factor	Dissipation Factor		IEC 60250	0.020

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	218 °C
	Heat distortion temperature		ISO 75-2/B	215 °C
		Heat distortion temperature		ASTM D648	210 °C
		Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	205 °C
melting temperature		ASTM D3418	220 °C
melting temperature	melting temperature		ISO 3146	220 °C
Linear coefficient of thermal expansion		ASTME831	3.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion			2.1E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion			7E-05 cm/cm/°C
RTI Elec		UL 746	130 °C
	RTI Elec		UL 746	140 °C
	RTI Elec	RTI Elec		UL 746	140 °C
RTI Imp		UL 746	115 °C
	RTI Imp		UL 746	115 °C
	RTI Imp	RTI Imp		UL 746	120 °C
RTI Str		UL 746	130 °C
	RTI Str		UL 746	140 °C
	RTI Str	RTI Str		UL 746	140 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.