Impact resistance	Test Condition	Test Method	BASF GERMANY/8233G MT7499
Charpy Notched Impact Strength	23°C	ISO 179	15 kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	110 J/m
Impact strength of cantilever beam gap		23°C	ASTM D256	150 J/m
Charpy Notched Impact Strength	-30°C	ISO 179	10 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	10 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180	8.5 kJ/m²
Dart impact	23°C	内部方法	4.07 J
Impact strength of simply supported beam without notch	23°C	ISO 179	88 kJ/m²

hardness	Test Condition	Test Method	BASF GERMANY/8233G MT7499
Rockwell hardness	R级	ASTM D785	121

Electrical performance	Test Condition	Test Method	BASF GERMANY/8233G MT7499
dielectric constant	100Hz	IEC 60250	4.20
dielectric strength		IEC 60243-1	44 KV/mm
Volume resistivity		IEC 60093	>1.0E+13 ohms·cm
Volume resistivity		1.50mm	ASTM D257	>1.0E+13 ohms·cm
Dissipation Factor	100Hz	IEC 60250	0.020
dielectric constant	1MHz	IEC 60250	3.60
Dissipation Factor	1MHz	IEC 60250	0.020

Mechanical properties	Test Condition	Test Method	BASF GERMANY/8233G MT7499
tensile strength	断裂,-40°C	ISO 527-2	283 Mpa
elongation	Break,121°C	ASTM D638	7.0 %
tensile strength	断裂,80°C	ISO 527-2	110 Mpa
Tensile modulus	80°C	ISO 527-2	4430 Mpa
Flexural modulus	-40°C	ASTM D790	9830 Mpa
bending strength	23°C	ASTM D790	297 Mpa
bending strength		65°C	ASTM D790	160 Mpa
Tensile modulus	23°C	ISO 527-2	10100 Mpa
tensile strength	断裂,80°C	ASTM D638	110 Mpa
tensile strength		断裂,23°C	ISO 527-2	185 Mpa
Tensile strain	断裂,-40°C	ISO 527-2	3.6 %
Tensile modulus	150°C	ISO 527-2	3440 Mpa
bending strength	121°C	ASTM D790	112 Mpa
Flexural modulus	90°C	ASTM D790	3750 Mpa
tensile strength	断裂,150°C	ISO 527-2	80.0 Mpa
Tensile strain	断裂,120°C	ISO 527-2	7.0 %
Flexural modulus	23°C	ISO 178	8200 Mpa
bending strength	-40°C	ASTM D790	380 Mpa
tensile strength	Break,121°C	ASTM D638	83.0 Mpa
Tensile strain	断裂,80°C	ISO 527-2	7.0 %
Tensile strain		断裂,150°C	ISO 527-2	6.0 %
Tensile modulus	-40°C	ISO 527-2	10500 Mpa
tensile strength	断裂,23°C	ASTM D638	195 Mpa
bending strength	90°C	ASTM D790	140 Mpa
Tensile modulus	120°C	ISO 527-2	3550 Mpa
tensile strength	断裂,120°C	ISO 527-2	83.0 Mpa
Tensile strain	断裂,23°C	ISO 527-2	3.5 %
bending strength	23°C	ISO 178	260 Mpa
Flexural modulus	121°C	ASTM D790	3320 Mpa
elongation	断裂,-40°C	ASTM D638	3.6 %
elongation		断裂,80°C	ASTM D638	7.0 %
Flexural modulus	65°C	ASTM D790	4020 Mpa
Flexural modulus		23°C	ASTM D790	9040 Mpa
tensile strength	断裂,-40°C	ASTM D638	283 Mpa
elongation	断裂,23°C	ASTM D638	3.5 %

flammability	Test Condition	Test Method	BASF GERMANY/8233G MT7499
UL flame retardant rating	3.0mm	UL 94	HB
		1.5mm	UL 94	HB
		0.60mm	UL 94	HB
		0.71mm	UL 94	HB

physical property	Test Condition	Test Method	BASF GERMANY/8233G MT7499
Shrinkage rate	MD：3.18mm		0.30 %
Water absorption rate	饱和	ASTM D570	6.4 %
		24hr	ASTM D570	1.1 %
		23°C,24hr	ISO 62	1.1 %
		平衡,50%RH	ASTM D570	1.8 %
		平衡,23°C,50%RH	ISO 62	1.8 %
		饱和,23°C	ISO 62	6.4 %
density		ASTM D792	1.39 g/cm³
density			ISO 1183	1.39 g/cm³

Thermal performance	Test Condition	Test Method	BASF GERMANY/8233G MT7499
Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	210 °C
RTI Imp	1.5mm	UL 746	115 °C
melting temperature		ASTM D3418	220 °C
RTI Elec	0.71mm	UL 746	130 °C
RTI Elec		3.0mm	UL 746	140 °C
RTI Imp	3.0mm	UL 746	120 °C
melting temperature		ISO 3146	220 °C
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	218 °C
Heat distortion temperature		0.45MPa,未退火，HDT	ISO 75-2/B	215 °C
Linear coefficient of thermal expansion	MD		2.1E-05 cm/cm/°C
Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	205 °C
RTI Str	1.5mm	UL 746	140 °C
RTI Str		3.0mm	UL 746	140 °C
RTI Elec	1.5mm	UL 746	140 °C
Linear coefficient of thermal expansion	MD	ASTME831	3.8E-05 cm/cm/°C
Linear coefficient of thermal expansion		TD		7E-05 cm/cm/°C
RTI Imp	0.71mm	UL 746	115 °C
RTI Str	0.71mm	UL 746	130 °C