PBT

PBT Crastin® 6129 NC010 DuPont, European Union

Unit Price:US$ 3,913 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Glass fiber reinforced
Application Areas:Electronic and electrical components｜Automotive Applications｜Non specific food applications
Color:--
Grade:Flame retardant grade

Material Certification

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Elongation at Break	23°C	ISO 527-2	>50 %
tensile strength	23°C	ISO 527-2	58.0 Mpa
Tensile modulus	23°C	ISO 527-2	2600 Mpa
Tensile creep modulus	1Hr	ISO 899-1	2600 Mpa
Tensile creep modulus	Tensile creep modulus	1000Hr	ISO 899-1	1800 Mpa
bending strength	23°C	ISO 178	85.0 Mpa
Bending modulus	23°C	ISO 178	2350 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0 kJ/m²

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.3E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.3E-04 cm/cm/°C
Vicat softening temperature	Melting Temperature	ISO 11357-3	225 °C
Vicat softening temperature	Vicat softening temperature		ISO 306/B50	175 °C
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	50.0 °C
	Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/A	60.0 °C
		Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	115 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPaAnnealed	ISO 75-2/B	180 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD2.0mm	ISO 294-4	1.7 %
Shrinkage rate	Shrinkage rate	MD2.0mm	ISO 294-4	1.5 %
density		ISO 1183	1.30 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	相对漏电起痕指数	IEC 60112	600 V
Dielectric strength		IEC 60243-1	26 KV/mm
Surface resistivity		IEC 60093	1E+12 Ω.cm
Volume resistivity		IEC 60093	>1.0E+15 Ω.cm

flame retardant performance	Test Condition	Test Method	Test Result
Relative temperature of heating wire	0.92mm	IEC 60695-2-13	925 °C
Ignition temperature of heating wire	3.00mm	IEC 60695-2-12	825 °C
	Ignition temperature of heating wire	1.50mm	IEC 60695-2-12	825 °C
	Ignition temperature of heating wire	Ignition temperature of heating wire	0.92mm	IEC 60695-2-12	825 °C
Extreme Oxygen Index		ISO 4589-2	22 %
UL flame retardant rating		UL -94	HB 3.00mm
	UL flame retardant rating		UL -94	HB 1.50mm
	UL flame retardant rating	UL flame retardant rating		UL -94	HB 0.92mm
Relative temperature of heating wire	1.50mm	IEC 60695-2-13	960 °C
Relative temperature of heating wire	Relative temperature of heating wire	3.00mm	IEC 60695-2-13	850 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Crastin® 6129 NC010 DuPont, European Union

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet