PBT 6129 NC010 PBT vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PBT DuPont, European Union 6129 NC010

Flame retardant grade

US$ 2,950 / MT

FOB Shenzhen Port

thermal performance	Test Condition	Test Method	DuPont, European Union/6129 NC010
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/A	60.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.3E-04 cm/cm/°C
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	115 °C
Hot deformation temperature		0.45MPaAnnealed	ISO 75-2/B	180 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.3E-04 cm/cm/°C
Vicat softening temperature	Melting Temperature	ISO 11357-3	225 °C
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	50.0 °C
Vicat softening temperature		ISO 306/B50	175 °C
flame retardant performance	Test Condition	Test Method	DuPont, European Union/6129 NC010
Extreme Oxygen Index		ISO 4589-2	22 %
Relative temperature of heating wire	0.92mm	IEC 60695-2-13	925 °C
Ignition temperature of heating wire	3.00mm	IEC 60695-2-12	825 °C
Ignition temperature of heating wire		0.92mm	IEC 60695-2-12	825 °C
Relative temperature of heating wire	1.50mm	IEC 60695-2-13	960 °C
Ignition temperature of heating wire	1.50mm	IEC 60695-2-12	825 °C
Relative temperature of heating wire	3.00mm	IEC 60695-2-13	850 °C
UL flame retardant rating		UL -94	HB 0.92mm
Physical properties	Test Condition	Test Method	DuPont, European Union/6129 NC010
density		ISO 1183	1.30 g/cm³
Shrinkage rate	MD2.0mm	ISO 294-4	1.5 %
Shrinkage rate		TD2.0mm	ISO 294-4	1.7 %
mechanical properties	Test Condition	Test Method	DuPont, European Union/6129 NC010
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.0 kJ/m²
tensile strength	23°C	ISO 527-2	58.0 Mpa
bending strength	23°C	ISO 178	85.0 Mpa
Tensile creep modulus	1000Hr	ISO 899-1	1800 Mpa
Elongation at Break	23°C	ISO 527-2	>50 %
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0 kJ/m²
Tensile creep modulus	1Hr	ISO 899-1	2600 Mpa
Bending modulus	23°C	ISO 178	2350 Mpa
Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.5 kJ/m²
Tensile modulus	23°C	ISO 527-2	2600 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.5 kJ/m²
Electrical performance	Test Condition	Test Method	DuPont, European Union/6129 NC010
Volume resistivity		IEC 60093	>1.0E+15 Ω.cm
Dissipation factor	相对漏电起痕指数	IEC 60112	600 V
Surface resistivity		IEC 60093	1E+12 Ω.cm
Dielectric strength		IEC 60243-1	26 KV/mm