PBT LNP™ THERMOCOMP™ WF1008-BK SABIC INNOVATIVE US
166
- Unit Price:US$ 3,910 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Aging resistance｜High mobility
- Application Areas:Electronic and electrical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 208 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 215 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 222 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 220 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 3.2E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 7.3E-05 cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD：24小时 | ASTM D955 | 0.30-0.60 % |
| TD：24hr | ASTM D955 | 1.0-4.0 % | |
| water absorption rate | 24hr,50%RH | ASTM D570 | 0.050 % |
| 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile modulus | ASTM D638 | 12500 Mpa | |
| ISO 527-2/1 | 13400 Mpa | ||
| tensile strength | 断裂 | ASTM D638 | 128 Mpa |
| 断裂 | ISO 527-2/5 | 134 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.4 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 11900 Mpa |
| ISO 178 | 11800 Mpa | ||
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 190 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.3 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 39 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 14.1 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.00 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.