PBT WF1008-BK SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical components
Aging resistance,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/WF1008-BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 39 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 14.1 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.00 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.3 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/WF1008-BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 13400 Mpa | |
| ASTM D638 | 12500 Mpa | ||
| tensile strength | 断裂 | ISO 527-2/5 | 134 Mpa |
| elongation | 断裂 | ASTM D638 | 2.4 % |
| Flexural modulus | ISO 178 | 11800 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| tensile strength | 断裂 | ASTM D638 | 128 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 11900 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 190 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/WF1008-BK |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.30-0.60 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.050 % |
| 平衡,23°C,50%RH | ISO 62 | 0.050 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 1.0-4.0 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/WF1008-BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 215 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 3.2E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 7.3E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 208 °C |
| 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 220 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 222 °C |