Material Description

Material Properties:High temperature resistance｜transparent
Application Areas:Electronic and electrical components
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ASTM D542	1.600
transmissivity	2540 μm	ASTM D1003	85.0 %
turbidity	2540 μm	ASTM D1003	1.0 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	13 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	46 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	11 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	35 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200 J/m
Dart impact	23°C	ASTM D3029	149 J
Impact strength of cantilever beam gap		ASTM D1822	577 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	2.0 mm	IEC 60695-2-12	850 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	2300 Mpa
tensile strength	Yield	ISO 527-2/50	70.0 Mpa
Tensile strain	Yield	ISO 527-2/50	7.0 %
Tensile strain	Tensile strain	Break	ISO 527-2/50	> 50 %
Bending modulus		ISO 178	2300 Mpa
tensile strength	Yield	ASTM D638	65.0 Mpa
tensile strength	tensile strength	Break	ASTM D638	77.0 Mpa
elongation	Break	ASTM D638	78 %
Bending modulus	50.0 mm Span	ASTM D790	2330 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	97.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			125 to 135 °C
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			300 to 320 °C
Temperature in the middle of the barrel			310 to 330 °C
Temperature at the front of the material cylinder			320 to 340 °C
Spray nozzle temperature			320 to 340 °C
Processing (melt) temperature			325 to 360 °C
Mold temperature			100 to 125 °C
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			325 to 350 °C
Temperature in the middle of the barrel			340 to 360 °C
Temperature at the front of the material cylinder			350 to 370 °C
Spray nozzle temperature			345 to 365 °C
Processing (melt) temperature			350 to 370 °C
Mold temperature			80 to 115 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	165 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	150 °C
Vicat softening temperature	--	ISO 306/A50	185 °C
	Vicat softening temperature	--	ISO 306/B50	175 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	170 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	23 to 80°C，Flow	ISO 11359-2	8.0E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.21 W/m/K
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	148 °C
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	8.1E-5 cm/cm/°C
specific heat		ASTM C351	1260 J/kg/°C
thermal conductivity		ASTM C177	0.21 W/m/K
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
RTI		UL 746	130 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	300°C/5.0 kg	ISO 1133	6.00 cm3/10min
Shrinkage rate	Flow	Internal Method	0.90 %
Specific volume		ASTM D792	0.830 cm³/g
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	2.0 g/10 min
melt mass-flow rate	melt mass-flow rate	300°C/6.1 kg	ASTM D1238	9.0 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.80 - 1.0 %
Water absorption rate	24 hr	ASTM D570	0.19 %

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	1 MHz	IEC 60250	3.10
Dissipation factor	100 Hz	IEC 60250	0.026
Volume resistivity		ASTM D257	> 2.5E+17 ohms·cm
Dielectric strength	3.20 mm, in Air	ASTM D149	20 KV/mm
Dielectric constant	60 Hz	ASTM D150	3.27
	Dielectric constant	50 kHz	ASTM D150	3.27
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.10
Dissipation factor	50 Hz	ASTM D150	1.6E-3
	Dissipation factor	60 Hz	ASTM D150	1.6E-3
	Dissipation factor	Dissipation factor	100 Hz	ASTM D150	0.026
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 3
High arc combustion index		UL 746	PLC 3
High voltage arc tracing rate		UL 746	PLC 3
Hot wire ignition		UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R -Sale	ISO 2039-2	127
	Rockwell hardness	M-Scale	ASTM D785	92
	Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	127

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ 4701R-110001 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet