Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 4701R-110001 SABIC INNOVATIVE US
LEXAN™
Electronic and electrical components
High temperature resistan,transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 46 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 13 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 11 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 35 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | ASTM D1822 | 577 kJ/m² | |
| Dart impact | 23°C | ASTM D3029 | 149 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 92 |
| R 计秤 | ISO 2039-2 | 127 | |
| R 级 | ASTM D785 | 127 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 70.0 Mpa |
| elongation | 断裂 | ASTM D638 | 78 % |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 97.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 77.0 Mpa |
| 屈服 | ASTM D638 | 65.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | > 50 % |
| 屈服 | ISO 527-2/50 | 7.0 % | |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2330 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 2.5E+17 ohms·cm | |
| Dissipation Factor | 50 Hz | ASTM D150 | 1.6E-3 |
| 100 Hz | IEC 60250 | 0.026 | |
| dielectric constant | 1 MHz | ASTM D150 | 3.10 |
| relative permittivity | 1 MHz | IEC 60250 | 3.10 |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 3 | |
| Dissipation Factor | 100 Hz | ASTM D150 | 0.026 |
| dielectric constant | 60 Hz | ASTM D150 | 3.27 |
| Dissipation Factor | 60 Hz | ASTM D150 | 1.6E-3 |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 20 KV/mm |
| arc resistance | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | |
| dielectric constant | 50 kHz | ASTM D150 | 3.27 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| refractive index | ASTM D542 | 1.600 | |
| transmissivity | 2540 µm | ASTM D1003 | 85.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| melt mass-flow rate | 300°C/6.1 kg | ASTM D1238 | 9.0 g/10 min |
| Melt volume flow rate | 300°C/5.0 kg | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | Flow | 内部方法 | 0.90 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.19 % |
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 2.0 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.80 - 1.0 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| Linear coefficient of thermal expansion | -40 到 95°C，流动 | ASTM E831 | 8.1E-5 cm/cm/°C |
| specific heat | ASTM C351 | 1260 J/kg/°C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI | UL 746 | 130 °C | |
| vicat | -- | ISO 306/B120 | 170 °C |
| thermal conductivity | ISO 8302 | 0.21 W/m/K | |
| ASTM C177 | 0.21 W/m/K | ||
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Be | 165 °C |
| vicat | -- | ISO 306/A50 | 185 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Ae | 150 °C |
| vicat | -- | ISO 306/B50 | 175 °C |
| RTI Imp | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | 23 到 80°C，流动 | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 148 °C |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/4701R-110001 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 350 to 370 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 340 to 360 °C | ||
| Temperature at the rear of the barrel | 325 to 350 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the front of the material cylinder | 350 to 370 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 80 to 115 °C | ||
| Spray nozzle temperature | 345 to 365 °C |