PA6

PA6 Amilan® CM1017XL3 TORAY JAPAN

251

Unit Price:US$ 3,287 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
61.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜Low temperature toughness｜Fast forming cycle
Application Areas:Automotive sector｜Shell｜Electrical components｜Electrical appliances
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-40°C		无断裂 --
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C		无断裂 --

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.79mm		V-2 --

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	80°C	MPa	25.0 20.0
	tensile strength	23°C	MPa	80.0 35.0
	tensile strength	tensile strength	-40°C		110 MPa
Rockwell hardness		ASTM D785	80
Tensile strain	Yield,23°C	%	1.5 --
Tensile strain	Tensile strain	Break,23°C	%	38
Bending modulus	-40°C	MPa	3800 3600
	Bending modulus	23°C		2800 MPa
	Bending modulus	Bending modulus	80°C	MPa	700 300
bending strength	-40°C		135 MPa
	bending strength	23°C	MPa	110 40.0
	bending strength	bending strength	80°C	MPa	40.0 25.0
Compressive stress	23°C	MPa	80.0 --
shear strength	23°C	MPa	70.0 65.0
Taber abraser	1000Cycles	mg	3.00to4.00 --
Friction coefficient vs. Metal			0.15to0.20 --

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		W/m/K	0.25 --
Melting temperature			225 ℃（℉）
Hot deformation temperature	0.45MPa,Unannealed	°C	182 --
Melting temperature		°C	225 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	8E-05 --
specific heat		J/kg/°C	1900 --

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	%	11 --
Water absorption rate	Water absorption rate	23°C,24hr	%	1.8 --
Shrinkage rate	MD：3.00mm4	%	1.2-1.8 --
Shrinkage rate	Shrinkage rate	MD：1.00mm3	%	0.70-1.1 --
Water absorption rate		ASTM D570/ISO 62	1.8 %
density		ASTM D792/ISO 1183	1.13

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	CTI	V	--
Arc resistance		sec	120 --
Dissipation factor	23°C,1MHz		0.030 0.13
	Dissipation factor	23°C,1kHz		0.060 0.11
	Dissipation factor	Dissipation factor	23°C,50Hz		0.070 0.10
Dielectric constant	23°C,1MHz		3.40 4.50
	Dielectric constant	23°C,1kHz		3.90 8.00
	Dielectric constant	Dielectric constant	23°C,50Hz		4.10 9.00
Dielectric strength		kV/mm	20 --
Volume resistivity		ohms·cm	1.0E+14-1.0E+15 1.0E+11到1.0E+12
Volume resistivity	Volume resistivity		ASTM D257/IEC 60093	10^12-13 Ω.cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,80°C		80 --
Rockwell hardness	Rockwell hardness	R-Sale,23°C		119

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.