Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1017XL3 TORAY JAPAN
Amilan®
Automotive sector、Shell、Electrical components、Electrical appliances
heat-resisting、Low temperature toughness、Fast forming cycle
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM1017XL3 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | 无断裂 -- | |
| -40°C | 无断裂 -- |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM1017XL3 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 119 | |
| R计秤,80°C | 80 -- |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM1017XL3 |
|---|---|---|---|
| Flexural modulus | -40°C | MPa | 3800 3600 |
| bending strength | 23°C | MPa | 110 40.0 |
| tensile strength | 23°C | MPa | 80.0 35.0 |
| bending strength | 80°C | MPa | 40.0 25.0 |
| Taber abraser | 1000Cycles | mg | 3.00to4.00 -- |
| compression stress | 23°C | MPa | 80.0 -- |
| Rockwell hardness | ASTM D785 | 80 | |
| tensile strength | -40°C | 110 MPa | |
| Flexural modulus | 23°C | 2800 MPa | |
| Tensile strain | 屈服,23°C | % | 1.5 -- |
| tensile strength | 80°C | MPa | 25.0 20.0 |
| Tensile strain | 断裂,23°C | % | 38 |
| shear strength | 23°C | MPa | 70.0 65.0 |
| Flexural modulus | 80°C | MPa | 700 300 |
| bending strength | -40°C | 135 MPa | |
| Friction coefficient - vs. Metal | 0.15to0.20 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM1017XL3 |
|---|---|---|---|
| arc resistance | sec | 120 -- | |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | -- |
| dielectric constant | 23°C,50Hz | 4.10 9.00 | |
| Dissipation Factor | 23°C,1kHz | 0.060 0.11 | |
| dielectric strength | kV/mm | 20 -- | |
| Dissipation Factor | 23°C,1MHz | 0.030 0.13 | |
| Volume resistivity | ohms·cm | 1.0E+14-1.0E+15 1.0E+11到1.0E+12 | |
| Dissipation Factor | 23°C,50Hz | 0.070 0.10 | |
| Volume resistivity | ASTM D257/IEC 60093 | 10^12-13 Ω.cm | |
| dielectric constant | 23°C,1kHz | 3.90 8.00 | |
| 23°C,1MHz | 3.40 4.50 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM1017XL3 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.8 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM1017XL3 |
|---|---|---|---|
| UL flame retardant rating | 0.79mm | V-2 -- |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM1017XL3 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | % | 11 -- |
| Shrinkage rate | MD：1.00mm3 | % | 0.70-1.1 -- |
| MD：3.00mm4 | % | 1.2-1.8 -- | |
| Water absorption rate | 23°C,24hr | % | 1.8 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM1017XL3 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 182 -- |
| melting temperature | °C | 225 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8E-05 -- |
| thermal conductivity | W/m/K | 0.25 -- | |
| specific heat | J/kg/°C | 1900 -- | |
| melting temperature | 225 ℃（℉） |