Material Properties:High impact resistance｜high definition｜heat-resisting｜high strength｜High mobility
Application Areas:Thin walled components｜sporting goods｜small home appliances｜Fitness equipment｜Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Electroplating grade

Material Certification

SGS

Technical Data Sheet Compare

physical property	Test Method	Test Result
density	ISO 1183	1.05 g/cm³
Melt volume flow rate	ISO 1133	32.0 cm3/10min
Shrinkage rate	ISO 294-4	0.40-0.60 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	107

Basic performance	Test Condition	Test Method	Test Result
melt mass-flow rate			32 g/10min

Mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength			28 KJ/m
Flexural modulus			2350 Mpa
Flexural modulus	Flexural modulus		ISO 178	2350 Mpa
bending strength		ISO 178	64.0 Mpa
Tensile modulus		ISO 527-2	2250 Mpa
tensile strength		ISO 527-2	40.0 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179	28 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature			80 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/Af	80.0 °C
Linear coefficient of thermal expansion		ISO 11359-2	8.5E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.