ABS 3001M UMG JAPAN
UMG ABS®
Thin walled components、sporting goods、small home appliances、Fitness equipment、Automotive sector、Electronic field、Electrical field
High impact resistance、high definition、heat-resisting、high strength、High mobility
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UMG JAPAN/3001M |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 11 kJ/m² |
| 23°C | ISO179 | 28 kJ/m² |
| hardness | Test Condition | Test Method | UMG JAPAN/3001M |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO2039-2 | 107 |
| Basic performance | Test Condition | Test Method | UMG JAPAN/3001M |
|---|---|---|---|
| melt mass-flow rate | 32 g/10min |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/3001M |
|---|---|---|---|
| Charpy impact strength | 28 KJ/m | ||
| Tensile modulus | 23°C | ISO527-2 | 2250 Mpa |
| Flexural modulus | 2350 Mpa | ||
| Bending modulus 2 | 23°C | ISO178 | 2350 Mpa |
| Bending stress 2 | 23°C | ISO178 | 64.0 Mpa |
| Tensile stress | 23°C | ISO527-2 | 40.0 Mpa |
| physical property | Test Condition | Test Method | UMG JAPAN/3001M |
|---|---|---|---|
| density | 23°C | ISO1183 | 1.05 g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 32.0 cm3/10min |
| Shrinkage rate | MD：23°C | ISO294-4 | 0.40到0.60 % |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/3001M |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/Af | 80.0 °C | |
| 80 °C | |||
| MD | ISO11359-2 | 8.5E-05 cm/cm/°C |