PC LEXAN™ HFD1810 NA9E108T SABIC INNOVATIVE NANSHA

320

Unit Price:US$ 5,120 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜copolymer
Application Areas:Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Light diffusion level

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.582
transmissivity	2540 μm	ASTM D1003	88.0	%
turbidity	2540 μm	ASTM D1003	< 1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	64	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	13	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	56.0	J
Dart impact	Dart impact	--	ISO 6603-2	95.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.30 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.0 mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span4	ASTM D790	100	Mpa
bending strength	bending strength	--5,6	ISO 178	91.0	Mpa
Bending modulus	--5	ISO 178	2180	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2240	Mpa
elongation	Break	ISO 527-2/50	97	%
	elongation	Break3	ASTM D638	130	%
		elongation	Yield	ISO 527-2/50	6.0	%
		elongation	elongation	Yield3	ASTM D638	5.5	%
tensile strength	Break	ISO 527-2/50	56.0	Mpa
	tensile strength	Break3	ASTM D638	56.0	Mpa
		tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	60.0	Mpa
Tensile modulus	--	ISO 527-2/1	2180	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2270	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature in the middle of the barrel			250 to 295	°C
Temperature at the front of the material cylinder			260 to 305	°C
drying temperature			105 to 110	°C
drying time			3.0 to 4.0	hr
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			240 to 280	°C
Spray nozzle temperature			255 to 300	°C
Processing (melt) temperature			260 to 305	°C
Mold temperature			50 to 80	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			35 to 75	rpm
Exhaust hole depth			0.038 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	121	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	110	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	115	°C
Vicat softening temperature	--	ASTM D152510	135	°C
	Vicat softening temperature	--	ISO 306/B50	129	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	130	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	8.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	8.0E-5	cm/cm/°C
RTI Elec		UL 746	105	°C
RTI Imp		UL 746	105	°C
RTI		UL 746	105	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.30	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	38.0	cm3/10min
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	40	g/10 min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Colorful	US$ 4700 /MT

Supplier Join

Get App

Top

PC LEXAN™ HFD1810 NA9E108T SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index