ASA Luran®S 797SE UV-WHP29435 INEOS STYRO KOREA
285
- Unit Price:US$ 2,143 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜High impact resistance
- Application Areas:Fitness equipment｜building materials｜Casters｜Profile｜Automotive sector｜Application in the automotive field｜sporting goods
- Color:--
- Grade:High impact resistance
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Pressure Test | ISO 2039-1 | 65.0 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Annealed | ISO 75-2/A | 95.0 °C |
| Vicat softening temperature | -- | ISO 306/A50 | 104 °C |
| -- | ISO 306/B50 | 90.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.0E-5to1.1E-4 cm/cm/°C |
| thermal conductivity | DIN 52612 | 0.17 W/m/K | |
| Hot deformation temperature | 0.45MPa,Annealed | ISO 75-2/B | 100 °C |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | Break | ISO 527-3 | 11 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | Saturation,23°C | ISO 62 | 1.7 % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.35 % | |
| density | ISO 1183 | 1.07 g/cm³ | |
| Apparent density | 0.59 g/cm³ | ||
| Melt Volume Flow Rate (MVR) | 220°C/10.0kg | ISO 1133 | 5.50 cm3/10min |
| Shrinkage rate | ISO 294-4 | 0.50-0.90 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface resistivity | IEC 60093 | 1E+13 ohms | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Dielectric constant | 100Hz | IEC 60250 | 3.80 |
| Dissipation factor | 100Hz | IEC 60250 | 9E-03 |
| 1MHz | IEC 60250 | 0.026 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2000 Mpa | |
| tensile strength | Yield,23°C | ISO 527-2 | 42.0 Mpa |
| Tensile strain | Yield,23°C | ISO 527-2 | 3.5 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1100 Mpa |
| bending strength | ISO 178 | 60.0 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179 | 9.0 kJ/m² |
| 23°C | ISO 179 | 40 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 10 kJ/m² |
| 23°C | ISO 180/A | 30 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.