Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA 797SE UV-WHP29435 INEOS STYRO KOREA
Luran®S
Fitness equipment,building materials,Casters,Profile,Automotive sector,Application in the automotive field,sporting goods
High mobility,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | INEOS STYRO KOREA/797SE UV-WHP29435 |
|---|---|---|---|
| Ball Pressure Test | ISO 2039-1 | 65.0 Mpa |
| thermal performance | Test Condition | Test Method | INEOS STYRO KOREA/797SE UV-WHP29435 |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Annealed | ISO 75-2/A | 95.0 °C |
| 0.45MPa,Annealed | ISO 75-2/B | 100 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.0E-5to1.1E-4 cm/cm/°C |
| thermal conductivity | DIN 52612 | 0.17 W/m/K | |
| Vicat softening temperature | -- | ISO 306/B50 | 90.0 °C |
| -- | ISO 306/A50 | 104 °C |
| film | Test Condition | Test Method | INEOS STYRO KOREA/797SE UV-WHP29435 |
|---|---|---|---|
| elongation | 断裂 | ISO 527-3 | 11 % |
| mechanical properties | Test Condition | Test Method | INEOS STYRO KOREA/797SE UV-WHP29435 |
|---|---|---|---|
| bending strength | ISO 178 | 60.0 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1100 Mpa |
| Tensile modulus | ISO 527-2 | 2000 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 3.5 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 42.0 Mpa |
| Electrical performance | Test Condition | Test Method | INEOS STYRO KOREA/797SE UV-WHP29435 |
|---|---|---|---|
| Dielectric constant | 100Hz | IEC 60250 | 3.80 |
| Dissipation factor | 1MHz | IEC 60250 | 0.026 |
| 100Hz | IEC 60250 | 9E-03 | |
| Surface resistivity | IEC 60093 | 1E+13 ohms | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm |
| Physical properties | Test Condition | Test Method | INEOS STYRO KOREA/797SE UV-WHP29435 |
|---|---|---|---|
| Apparent density | 0.59 g/cm³ | ||
| density | ISO 1183 | 1.07 g/cm³ | |
| Melt Volume Flow Rate (MVR) | 220°C/10.0kg | ISO 1133 | 5.50 cm3/10min |
| Shrinkage rate | ISO 294-4 | 0.50-0.90 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 1.7 % |
| 平衡,23°C,50%RH | ISO 62 | 0.35 % |
| impact performance | Test Condition | Test Method | INEOS STYRO KOREA/797SE UV-WHP29435 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179 | 9.0 kJ/m² |
| 23°C | ISO 179 | 40 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 10 kJ/m² |
| 23°C | ISO 180/A | 30 kJ/m² |