ABS TAITALAC® 5000M TAIDA TAIWAN
333
- Unit Price:US$ 1,495 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High rigidity｜High gloss｜Impact resistance｜High gloss ｜hard｜Impact resistance｜High rigidity｜Highlight｜Moderate impact resistance
- Application Areas:Household goods｜Video tape
- Color:--
- Grade:Extrusion grade
Material Certification
TDS
TDS_ISO
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 115 R |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Annealed, 12.7 mm | ASTM D648 | 85 °C |
| Vicat softening temperature | ASTM D1525 | 103 °C | |
| High arc combustion index | 1.57 mm | UL 746 | PLC 0 |
| High voltage arc tracing rate | 1.57 mm | UL 746 | mm/min |
| Hot wire ignition | 1.57 mm | UL 746 | PLC 3 sec |
| UL flame retardant rating | 1.59 mm | UL 94 | HB |
| Hot deformation temperature | 1.80MPaUnannealed | ASTM D648 | 85 °C |
| Vicat softening temperature | ASTM1525 | 103 °C |
| flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 200℃/5.0 kg | ASTM D1238 | 1.8 g/10 min |
| 220℃/10.0 kg | ASTM D1238 | 20 g/10 min | |
| Shrinkage rate | MD | ASTM D955 | < 0.40 % |
| Water absorption rate | Saturation | ASTM D570 | < 0.30 % |
| Shrinkage rate | MD | ASTM D995 | <0.40 % |
| Water absorption rate | (23°C,24hr) | ASTM D570 | <0.30 % |
| melt mass-flow rate | 200℃/5.0Kg | ASTM D1238 | 1.8 g/10min |
| 220℃/10.0Kg | ASTM D1238 | 20 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+22 Ω.cm | |
| Dielectric strength | ASTM D149 | 22 KV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | Yield, 23℃ | ASTM D790 | 77.5 Mpa |
| Impact strength of cantilever beam gap | 23℃, 3.18 mm | ASTM D256 | 200 J/m |
| 23℃, 6.35 mm | ASTM D256 | 180 J/m | |
| Rockwell hardness | R-Scale, 23℃ | ASTM D785 | 115 |
| tensile strength | Yield, 23℃, 3.18 mm | ASTM D638 | 44.1 Mpa |
| Break, 23℃, 3.18 mm | ASTM D638 | 37.3 Mpa | |
| elongation | Break, 23℃, 3.18 mm | ASTM D638 | 30 % |
| Elongation at Break | 23°C | ASTM D638 | 30 % |
| bending strength | 23°C | ASTM D790 | 76 Mpa |
| Bending modulus | 23°C | ASTM D790 | 2550 Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 220 J/m |
| tensile strength | 23°C | ASTM D638 | 44 Mpa |
| Bending modulus | 23℃ | ASTM D790 | 27000 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.