ABS 5000M TAIDA TAIWAN
TAITALAC®
Household goods,Video tape
High rigidity,High gloss,Impact resistance,High gloss ,hard,Impact resistance,High rigidity,Highlight,Moderate impact resistanc
RoHS
TDS
TDS_ISO
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TAIDA TAIWAN/5000M |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 115 R |
| Mechanical properties | Test Condition | Test Method | TAIDA TAIWAN/5000M |
|---|---|---|---|
| tensile strength | 断裂, 23℃, 3.18 mm | ASTM D638 | 37.3 Mpa |
| Flexural modulus | 23℃ | ASTM D790 | 27000 Mpa |
| tensile strength | 屈服, 23℃, 3.18 mm | ASTM D638 | 44.1 Mpa |
| bending strength | 23°C | ASTM D790 | 76 Mpa |
| elongation | 断裂, 23℃, 3.18 mm | ASTM D638 | 30 % |
| Rockwell hardness | R 级, 23℃ | ASTM D785 | 115 |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 220 J/m |
| 23℃, 6.35 mm | ASTM D256 | 180 J/m | |
| 23℃, 3.18 mm | ASTM D256 | 200 J/m | |
| bending strength | 屈服, 23℃ | ASTM D790 | 77.5 Mpa |
| elongation at break | 23°C | ASTM D638 | 30 % |
| Flexural modulus | 23°C | ASTM D790 | 2550 Mpa |
| tensile strength | 23°C | ASTM D638 | 44 Mpa |
| Electrical performance | Test Condition | Test Method | TAIDA TAIWAN/5000M |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+22 Ω.cm | |
| dielectric strength | ASTM D149 | 22 KV/mm |
| Flame retardant performance | Test Condition | Test Method | TAIDA TAIWAN/5000M |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm |
| physical property | Test Condition | Test Method | TAIDA TAIWAN/5000M |
|---|---|---|---|
| melt mass-flow rate | 200℃/5.0 kg | ASTM D1238 | 1.8 g/10 min |
| Shrinkage rate | MD | ASTM D955 | < 0.40 % |
| Water absorption rate | 饱和 | ASTM D570 | < 0.30 % |
| melt mass-flow rate | 200℃/5.0Kg | ASTM D1238 | 1.8 g/10min |
| Shrinkage rate | MD | ASTM D995 | <0.40 % |
| Water absorption rate | (23°C,24hr) | ASTM D570 | <0.30 % |
| melt mass-flow rate | 220℃/10.0Kg | ASTM D1238 | 20 g/10min |
| 220℃/10.0 kg | ASTM D1238 | 20 g/10 min |
| Thermal performance | Test Condition | Test Method | TAIDA TAIWAN/5000M |
|---|---|---|---|
| vicat | ASTM D1525 | 103 °C | |
| Heat distortion temperature | 1.8 MPa, 退火, 12.7 mm，HDT | ASTM D648 | 85 °C |
| vicat | ASTM1525 | 103 °C | |
| High Voltage Arc Traceability Rate (HVTR) | 1.57 mm | UL 746 | mm/min |
| Hot wire ignition (HWI) | 1.57 mm | UL 746 | PLC 3 sec |
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 85 °C |
| UL flame retardant rating | 1.59 mm | UL 94 | HB |
| High arc combustion index (HAI) | 1.57 mm | UL 746 | PLC 0 |