'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
POM TENAC™ 5010 ASAHI JAPAN
13
- Unit Price:US$ 4,940 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Shanghai Huibao Material Technology Co., Ltd
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Medium viscosity
- Application Areas:Engine parts｜Cam｜Electronic field｜Electrical field｜Shell｜currency｜Engineering accessories
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| other | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| characteristic | 中粘度 | |||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5mm | UL 94 | HB | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | ASTM D790/ISO 178 | 103 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 3040 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 94 | ||
| elongation | ASTM D638/ISO 527 | 45 | % | |
| tensile strength | ASTM D638/ISO 527 | 69 | kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 69 | kg·cm/cm(J/M)ft·lb/in | |
| Wear resistance | ASTM D1044 | 13 | ||
| Rockwell hardness | ASTM D785 | 120 | R | |
| Impact strength of cantilever beam gap | ASTM D256 | 69 | J/m | |
| Bending modulus | ASTM D790 | 3040 | Mpa | |
| bending strength | ASTM D790 | 103 | Mpa | |
| Elongation at Break | ASTM D638 | 45 | % | |
| tensile strength | ASTM D638 | 69 | Mpa | |
| Tensile modulus | ISO 527-2 | 3300 | Mpa | |
| tensile strength | Yield | ISO 527-2 | 72.0 | Mpa |
| -- | ASTM D638 | 72.0 | Mpa | |
| elongation | Break | ASTMD638 | 30 | % |
| Bending modulus | -- | ASTM D790 | 3040 | Mpa |
| -- | ISO 178 | 3100 | Mpa | |
| bending strength | ASTM D790 | 107 | Mpa | |
| Taber abraser | ASTM D1044 | 13.0 | mg | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 136(1.8Mpa) | ℃（℉） |
| Combustibility (rate) | UL 94 | HB | ||
| melt mass-flow rate | ASTM D1238 | 22 | g/10min | |
| UL flame retardant rating | UL 94 | HB | ||
| Hot deformation temperature | 0.45MPa | ASTM D648 | 172 | °C |
| 1.82MPa | ASTM D648 | 136 | °C | |
| Linear coefficient of thermal expansion | 10 | |||
| Hot deformation temperature | 0.45MPa,Unannealed | ASTM D648 | 172 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 165 | °C | |
| 1.8MPa,Unannealed | ASTM D648 | 136 | °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 105 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 | cm/cm/°C |
| specific heat | 1470 | J/kg/°C | ||
| thermal conductivity | 0.23 | W/m/K | ||
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ASTM D792/ISO 1183 | 1.42 | ||
| Shrinkage rate | Across Flow | 1.8-2.2 | % | |
| Flow | 1.8-2.2 | % | ||
| Water absorption rate | ASTM D570 | 0.2 | % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 22 | g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 | % | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 22 | g/10min |
| Shrinkage rate | MD | Internal Method | 1.8-2.2 | % |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | ASTM D257 | 1.0E+16-1.0E+17 | ohms | |
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15-1.0E+16 | ohms·cm |
| Dielectric strength | ASTM D149 | 18 | KV/mm | |
| Dielectric constant | 23°C,1MHz | ASTM D150 | 3.80 | |
| Dissipation factor | 23°C,1MHz | ASTM D150 | 7E-03 | |
| Arc resistance | ASTM D495 | 250 | sec | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ASTM D785 | 94 | |
| R-Scale | ASTM D785 | 120 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.