POM ASAHI JAPAN 5010

Injection grade

US$ 3,970 / MT

FOB Guangzhou port, China

Physical properties	Test Condition	Test Method	ASAHI JAPAN/5010
Water absorption rate		ASTM D570	0.2 %
melt mass-flow rate	190°C/2.16kg	ISO 1133	22 g/10min
melt mass-flow rate			ASTM D1238/ISO 1133	22 g/10min
Shrinkage rate	MD	Internal Method	1.8-2.2 %
density		ASTM D792/ISO 1183	1.42
Water absorption rate		ASTM D570/ISO 62	0.2 %
Water absorption rate		23°C,24hr,50%RH	ASTM D570	0.20 %
Shrinkage rate	Flow		1.8-2.2 %
Shrinkage rate		Across Flow		1.8-2.2 %
other	Test Condition	Test Method	ASAHI JAPAN/5010
characteristic			中粘度
mechanical properties	Test Condition	Test Method	ASAHI JAPAN/5010
Bending modulus	--	ISO 178	3100 Mpa
Elongation at Break		ASTM D638	45 %
tensile strength		ASTM D638	69 Mpa
Tensile modulus		ISO 527-2	3300 Mpa
bending strength		ASTM D790/ISO 178	103 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	69 kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	120
Wear resistance		ASTM D1044	13
tensile strength	--	ASTM D638	72.0 Mpa
Bending modulus		ASTM D790/ISO 178	3040 kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	45 %
bending strength		ASTM D790	107 Mpa
Taber abraser		ASTM D1044	13.0 mg
Bending modulus		ASTM D790	3040 Mpa
tensile strength	Yield	ISO 527-2	72.0 Mpa
Bending modulus	--	ASTM D790	3040 Mpa
elongation	Break	ASTMD638	30 %
Impact strength of cantilever beam gap		ASTM D256	69 J/m
tensile strength		ASTM D638/ISO 527	69 kg/cm²(MPa)[Lb/in²]
Electrical performance	Test Condition	Test Method	ASAHI JAPAN/5010
Surface resistivity		ASTM D257	1.0E+16-1.0E+17 ohms
Dielectric constant	23°C,1MHz	ASTM D150	3.80
Dielectric strength		ASTM D149	18 KV/mm
Dissipation factor	23°C,1MHz	ASTM D150	7E-03
Arc resistance		ASTM D495	250 sec
Volume resistivity	23°C	ASTM D257	1.0E+15-1.0E+16 ohms·cm
thermal performance	Test Condition	Test Method	ASAHI JAPAN/5010
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	172 °C
thermal conductivity			0.23 W/m/K
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	105 °C
Hot deformation temperature		HDT	ASTM D648/ISO 75	136(1.8Mpa) ℃（℉）
specific heat			1470 J/kg/°C
Hot deformation temperature	1.82MPa	ASTM D648	136 °C
melt mass-flow rate		ASTM D1238	22 g/10min
Hot deformation temperature	0.45MPa	ASTM D648	172 °C
Linear coefficient of thermal expansion	MD	ASTMD696	1E-04 cm/cm/°C
Linear coefficient of thermal expansion				10
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	165 °C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	136 °C
Combustibility (rate)		UL 94	HB
flammability	Test Condition	Test Method	ASAHI JAPAN/5010
UL flame retardant rating	1.5mm	UL 94	HB
hardness	Test Condition	Test Method	ASAHI JAPAN/5010
Rockwell hardness	R-Scale	ASTM D785	120
Rockwell hardness		M-Scale	ASTM D785	94