PC/ABS CYCOLAC™ LG8002 SABIC INNOVATIVE US
167
- Unit Price:US$ 4,041 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low gloss｜developable ｜High impact
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 注射成型 | ||
| characteristic | 低光泽.高冲击.延展性.紫外线稳定。适用于：汽车 | ||
| Color | 本色 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | -- kg·cm/cm(J/M)ft·lb/in | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 65 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 59 kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | -- kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | -- % | |
| Tensile modulus | ASTM D638/ISO 527 | -- kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 560 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 5.0 % | |
| Rockwell hardness | ASTM D785 | -- | |
| Flexural modulus | ASTM D790/ISO 178 | 23200 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 870 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 120 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | -- Ω | |
| dielectric constant | ASTM D150/IEC 60250 | -- | |
| arc resistance | ASTM D495/IEC 60112 | -- | |
| Volume resistivity | ASTM D257/IEC 60093 | -- Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13 | |
| Shrinkage rate | ASTM D955 | 0.50-0.70 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 260℃/5.0Kg.6.5 g/10min | |
| ASTM D1238/ISO 1133 | -- g/10min | ||
| Water absorption rate | ASTM D570/ISO 62 | -- % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | -- | |
| Heat distortion temperature | ASTM D648/ISO 75 | -- ℃（℉） | |
| ASTM D648/ISO 75 | 0.45MPa/3.20mm.121℃;1.80MPa/3.20mm.104℃ ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | -- ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.000090 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.