plas
Log In | Sign Up
CategoriesAll
Plastic Raw Materials
Modified Plastics
Plastic Additives
Color Masterbatch
Plastic Datasheets
Plastic News
About Us
Home
Plastic Raw Materials
PC

PC LEXAN™  HPS6R-1125 SABIC INNOVATIVE CANADA

223
  • Unit Price:US$ 4,565 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    20MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility
  • Application Areas:medical care｜medicine
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA15 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA75 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A70 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Dart impact23°C,EnergyatPeakLoadASTM D376365.0 J
Dart impact23°C,TotalEnergyASTM D376365.0 J
mechanical propertiesTest ConditionTest MethodTest Result
elongationBreakASTM D638140 %
Tensile strainYieldISO 527-2/506.0 %
elongationYieldASTM D6386.5 %
tensile strengthBreakISO 527-2/5075.0 Mpa
tensile strengthBreakASTM D63868.9 Mpa
tensile strengthYieldISO 527-2/5060.0 Mpa
tensile strengthYieldASTM D63862.1 Mpa
Tensile modulusISO 527-2/12300 Mpa
Tensile modulusASTM D6382310 Mpa
Tensile strainBreakISO 527-2/50140 %
Bending modulus50.0mmSpanASTM D7902340 Mpa
Bending modulusISO 1782250 Mpa
bending strengthISO 17895.0 Mpa
bending strengthYield,50.0mmSpanASTM D79097.9 Mpa
thermal performanceTest ConditionTest MethodTest Result
Vicat softening temperatureASTM D152511154 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af124 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648132 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648124 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648138 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-26E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8315.7E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B50143 °C
Vicat softening temperature--ISO 306/B120140 °C
Ball Pressure Test75°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to40°CASTME8316.2E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-26E-05 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648135 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Water absorption rateSaturation,23°CISO 620.35 %
Water absorption rate24hrASTM D5700.15 %
Shrinkage rateTD：3.20mmInternal Method0.50-0.70 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Shrinkage rateMD：--2Internal Method0.50-0.70 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11336.50 cm3/10min
melt mass-flow rate300°C/5.0kgASTM D1238110 g/10min
melt mass-flow rate300°C/1.2kgASTM D12387.0 g/10min
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785118
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.