PC HPS6R-1125 SABIC INNOVATIVE CANADA
LEXAN™
medical care,medicine
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HPS6R-1125 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 75 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 65.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 70 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 65.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HPS6R-1125 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HPS6R-1125 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.5 % |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 2340 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 75.0 Mpa |
| Tensile modulus | ASTM D638 | 2310 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| elongation | 断裂 | ASTM D638 | 140 % |
| tensile strength | Break | ASTM D638 | 68.9 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 97.9 Mpa |
| ISO 178 | 95.0 Mpa | ||
| Flexural modulus | ISO 178 | 2250 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 62.1 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 140 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HPS6R-1125 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 110 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 6.50 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Shrinkage rate | MD：--2 | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HPS6R-1125 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 132 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 6.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 135 °C |
| vicat | ASTM D152511 | 154 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 138 °C |
| vicat | -- | ISO 306/B120 | 140 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 5.7E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 143 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 124 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 124 °C |