Material Properties:Low temperature resistance｜wear resistant｜Filler: Glass fiber reinforced material｜50% filler by weight
Application Areas:Automotive components｜Electronic and electrical components
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	255 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	246 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	61 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	275°C/2.16kg	ISO 1133	4.6 g/10min
Melt volume flow rate	275°C/2.16kg	ISO 1133	2.70 cm3/10min
shrinkage rate			0.23 %
Water absorption rate	饱和,23°C	ISO 62	0.10 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.90 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	19700 Mpa
tensile strength	断裂	ISO 527-2	250 Mpa
Tensile strain	断裂	ISO 527-2	1.9 %
flexural modulus		ISO 178	18700 Mpa
bending strength		ISO 178	382 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.