Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 G-09S BLK01 MITSUBISHI ENGINEERING JAPAN
RENY™
Automotive components,Electronic and electrical components
Low temperature resistanc,wear resistant,Filler: Glass fiber reinf,50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/G-09S BLK01 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 61 kJ/m² |
| thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/G-09S BLK01 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 255 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 246 °C |
| mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/G-09S BLK01 |
|---|---|---|---|
| bending strength | ISO 178 | 382 Mpa | |
| flexural modulus | ISO 178 | 18700 Mpa | |
| Tensile modulus | ISO 527-2 | 19700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.9 % |
| tensile strength | 断裂 | ISO 527-2 | 250 Mpa |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/G-09S BLK01 |
|---|---|---|---|
| melt mass-flow rate | 275°C/2.16kg | ISO 1133 | 4.6 g/10min |
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 2.70 cm3/10min |
| shrinkage rate | 0.23 % | ||
| Water absorption rate | 饱和,23°C | ISO 62 | 0.10 % |
| 平衡,23°C,50%RH | ISO 62 | 0.90 % |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/G-09S BLK01 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |