PC TARFLON™ GZ-2510 IDEMITSU JAPAN
203
- Unit Price:US$ 3,769 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Bromine free｜Flame retardant｜Glass fiber reinforced material｜Filler: Glass fiber reinforced material｜10% filler by weight｜10% filler by weight｜Phosphorus content｜Low (to none)｜Bromine free｜Flame retardant performance
- Application Areas:Industrial applications｜Fitness equipment｜Printing machine parts｜LCD application｜LCD application｜Power/Other Tools｜model｜Printing machine parts
- Color:--
- Grade:Extrusion grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.27 g/cm³ | |
| Shrinkage rate | 内部方法 | 0.6 % | |
| 内部方法 | 0.4 % | ||
| Water absorption rate | ISO 62 | 0.15 % | |
| density | ISO 1183 | 1.27 g/cm³ | |
| spiral flow length | 内部方法 | 21.0 CM | |
| Shrinkage rate | 内部方法 | 0.60 % | |
| 内部方法 | 0.40 % | ||
| Water absorption rate | ISO 62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 65 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO Shortcut | >PC-GF10< |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 65 | |
| tensile strength | ISO 527-2 | 80 Mpa | |
| Tensile strain | ISO 527-2 | 5 % | |
| Flexural modulus | ISO 178 | 3500 Mpa | |
| bending strength | ISO 178 | 120 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 8 kJ/m² | |
| tensile strength | ISO 527-2 | 80.0 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 5.0 % | |
| Flexural modulus | ISO 178 | 3500 Mpa | |
| bending strength | ISO 178 | 120 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 8.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | IEC 60250 | 2.95 | |
| arc resistance | ASTM D495 | 110 sec | |
| dielectric strength | IEC 60243-1 | > 22 KV/mm | |
| Volume resistivity | ASTM D257 | >1.0E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | >22 KV/mm | |
| dielectric constant | IEC 60250 | 2.95 | |
| Dissipation Factor | IEC 60250 | 9E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 142 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 0.000045 cm/cm/℃ | |
| UL flame retardant rating | UL 94 | V-0 | |
| Heat distortion temperature | ISO 75-2/A | 142 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 4.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.