Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GZ-2510 IDEMITSU JAPAN
TARFLON™
Industrial applications、Fitness equipment、Printing machine parts、LCD application、LCD application、Power/Other Tools、model、Printing machine parts
Glass fiber reinforced、Bromine free、Flame retardant、Glass fiber reinforced ma、Filler: Glass fiber reinf、10% filler by weight、10% filler by weight、Phosphorus content、Low (to none)、Bromine free、Flame retardant performan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/GZ-2510 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/GZ-2510 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 65 |
| Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/GZ-2510 |
|---|---|---|---|
| ISO Shortcut | >PC-GF10< |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/GZ-2510 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 5.0 % | |
| bending strength | ISO 178 | 120 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 8 kJ/m² | |
| Tensile strain | 断裂 | ISO 527-2 | 5 % |
| Flexural modulus | ISO 178 | 3500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 80 Mpa |
| 屈服 | ISO 527-2 | 80.0 Mpa | |
| Rockwell hardness | M 计秤 | ISO 2039-2 | 65 |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/GZ-2510 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | >22 KV/mm | |
| dielectric constant | 1MHz | IEC 60250 | 2.95 |
| 1 MHz | IEC 60250 | 2.95 | |
| arc resistance | ASTM D495 | 110 sec | |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/GZ-2510 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/GZ-2510 |
|---|---|---|---|
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.60 % |
| spiral flow length | 内部方法 | 21.0 CM | |
| Shrinkage rate | MD: 2.00 mm | 内部方法 | 0.4 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Shrinkage rate | TD | 内部方法 | 0.6 % |
| density | ISO 1183 | 1.27 g/cm³ | |
| Shrinkage rate | MD:2.00mm | 内部方法 | 0.40 % |
| Water absorption rate | 平衡, 23℃, 50% RH | ISO 62 | 0.15 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/GZ-2510 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 142 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 142 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.5E-05 cm/cm/°C |
| UL flame retardant rating | 1.50 mm | UL 94 | V-0 |
| Linear coefficient of thermal expansion | ASTM D696 | 0.000045 cm/cm/℃ |