PPA AKROLOY® PA GF 50 BK AKRO-PLASTIC GERMANY

450

Unit Price:US$ 4,630 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	110	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	95	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00 mm	FMVSS 302	< 100	mm/min
UL flame retardant rating	0.8 mm	UL 94	HB
Burning wire flammability index	1.6 mm	IEC 60695-2-12	700	°C
filler content		ISO 1172	50	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	380	Mpa
Bending modulus		ISO 178	16400	Mpa
Tensile strain	Break	ISO 527-2/5	3.0	%
tensile strength	Break	ISO 527-2/5	250	Mpa
Tensile modulus		ISO 527-2/1	17500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Temperature index - at 50% loss of tensile strength			140 to 150	°C
Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength			110 to 130	°C
Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	6.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	1.5E-5	cm/cm/°C
Melting temperature		DIN EN 11357-1	255	°C
Vicat softening temperature		ISO 306/B50	242	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	225	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	245	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Humidity Absorption - 62% RH	70°C	ISO 1110	1.1	%
Water absorption rate	Saturation, 23°C	ISO 62	3.5 to 4.0	%
Shrinkage rate	Flow	ISO 294-4	0.50	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.50	%
Spiral flow length		Internal Method	54.0	CM
Melt Volume Flow Rate (MVR)	275°C/5.0 kg	ISO 1133	9.00	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	1 MHz	IEC 60250	4.42
Surface resistivity		IEC 60093	1.5E+17	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H 961/30	ISO 2039-1	290	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPA AKROLOY® PA GF 50 BK AKRO-PLASTIC GERMANY

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index