PC/ABS INFINO® NH-1013 K24806 Samsung Cheil South Korea

238

Unit Price:US$ 2,916 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.2 mm	UL 94	V-1
	UL flame retardant rating	1.530mm	UL 94	V-0
		UL flame retardant rating	2.030mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
bending strength	--5	ISO 178	90.0 Mpa
bending strength	bending strength	--4	ASTM D790	90.0 Mpa
Bending modulus	--5	ISO 178	2650 Mpa
Bending modulus	Bending modulus	--4	ASTM D790	2500 Mpa
elongation	Break	ISO 527-2/50	60 %
elongation	elongation	Break3	ASTM D638	50 %
tensile strength	Break	ISO 527-2/50	50.0 Mpa
	tensile strength	Break3	ASTM D638	59.0 Mpa
		tensile strength	Yield	ISO 527-2/50	60.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	62.0 Mpa

injection	Test Condition	Test Method	Test Result
Hot air dryer			80 °C
Vacuum drying machine			80 °C
Hot air dryer			2.0 to 4.0 hr
Vacuum drying machine			> 4.0 hr
Suggested maximum moisture content			< 0.050 %
Temperature at the rear of the barrel			230 to 250 °C
Temperature in the middle of the barrel			240 to 260 °C
Temperature at the front of the material cylinder			250 to 270 °C
Spray nozzle temperature			270 °C
Mold temperature			50 to 70 °C
Injection pressure			98.1 Mpa
Back pressure			0.490 to 1.96 Mpa
Screw speed			50 to 150 rpm

thermal performance	Test Condition	Test Method	Test Result
RTI	1.5 to 3.0 mm	UL 746	90.0 °C
RTI Imp	1.5 to 3.0 mm	UL 746	85.0 °C
RTI Elec	1.5 to 3.0 mm	UL 746	90.0 °C
Vicat softening temperature		ISO 306/B50	100 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	82.0 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	88.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.40 - 0.70 %
	Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.40 - 0.70 %
		Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.40 - 0.70 %
		Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.40 - 0.70 %
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	33 g/10 min

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index	1.5 mm	UL 746	PLC 3
Compared to the anti leakage trace index		IEC 60112	PLC 0
Hot wire ignition	1.5 mm	UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R -Sale	ISO 2039-2	118
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.