PC/ABS NH-1013 K24806 Samsung Cheil South Korea
INFINO®
--
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/NH-1013 K24806 |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 118 |
| R 级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/NH-1013 K24806 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| 屈服3 | ASTM D638 | 62.0 Mpa | |
| elongation | 断裂3 | ASTM D638 | 50 % |
| bending strength | --4 | ASTM D790 | 90.0 Mpa |
| --5 | ISO 178 | 90.0 Mpa | |
| elongation | 断裂 | ISO 527-2/50 | 60 % |
| Flexural modulus | --4 | ASTM D790 | 2500 Mpa |
| --5 | ISO 178 | 2650 Mpa | |
| tensile strength | 断裂3 | ASTM D638 | 59.0 Mpa |
| 断裂 | ISO 527-2/50 | 50.0 Mpa |
| Electrical performance | Test Condition | Test Method | Samsung Cheil South Korea/NH-1013 K24806 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Hot wire ignition (HWI) | 1.5 mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.5 mm | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/NH-1013 K24806 |
|---|---|---|---|
| UL flame retardant rating | 1.530mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | 5VA | |
| 2.030mm | UL 94 | 5VB | |
| 1.2 mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/NH-1013 K24806 |
|---|---|---|---|
| Shrinkage rate | 横向流动 : 3.20 mm | ASTM D955 | 0.40 - 0.70 % |
| 流量 : 2.00 mm | ISO 294-4 | 0.40 - 0.70 % | |
| 流动 : 3.20 mm | ASTM D955 | 0.40 - 0.70 % | |
| 横向流量 : 2.00 mm | ISO 294-4 | 0.40 - 0.70 % | |
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238 | 33 g/10 min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/NH-1013 K24806 |
|---|---|---|---|
| vicat | ISO 306/B50 | 100 °C | |
| RTI Elec | 1.5 到 3.0 mm | UL 746 | 90.0 °C |
| RTI | 1.5 到 3.0 mm | UL 746 | 90.0 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/A | 82.0 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 88.0 °C | |
| RTI Imp | 1.5 到 3.0 mm | UL 746 | 85.0 °C |
| injection | Test Condition | Test Method | Samsung Cheil South Korea/NH-1013 K24806 |
|---|---|---|---|
| screw speed | 50 to 150 rpm | ||
| Suggested maximum moisture content | < 0.050 % | ||
| Vacuum dryer | 80 °C | ||
| Injection Pressure | 98.1 Mpa | ||
| Hot air dryer | 2.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 240 to 260 °C | ||
| Temperature at the rear of the barrel | 230 to 250 °C | ||
| Vacuum dryer | > 4.0 hr | ||
| Temperature at the front of the material cylinder | 250 to 270 °C | ||
| Back pressure | 0.490 to 1.96 Mpa | ||
| Temperature | 50 to 70 °C | ||
| Hot air dryer | 80 °C | ||
| Spray nozzle temperature | 270 °C |