plas
Log In | Sign Up
CategoriesAll
Plastic Raw Materials
Modified Plastics
Plastic Additives
Color Masterbatch
Plastic Datasheets
Plastic News
About Us
Home
Plastic Raw Materials
PBT

PBT Crastin®  SO653 NC010 DuPont, European Union

183
  • Unit Price:US$ 3,664 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    30MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low warpage｜Filler: Glass beads｜20% filler by weight
  • Application Areas:Electronic and electrical components｜Automotive Applications
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

Other performanceTest ConditionTest MethodTest Result
Extreme Oxygen IndexISO 4589-122 %
impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA3.5 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA3.5 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU50 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU40 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A4.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A3.5 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U34 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U37 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Burning rate1.00mmISO 379524 mm/min
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating3.0mmUL 94HB
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
UL flame retardant rating3.0mmIEC 60695-11-10,-20HB
Extreme Oxygen IndexISO 4589-222 %
FMVSS flammabilityFMVSS302SE/B
Fogging-G-valuecondensateISO 64521E-04 g
mechanical propertiesTest ConditionTest MethodTest Result
Tensile creep modulus1hISO 899-13500 MPa
Tensile creep modulus1000hISO 899-12400 MPa
Impact strength of simply supported beam without notch23℃, Type 1, EdgewiseISO 17940 KJ/m
Charpy Notched Impact Strength-30℃, Type 1, Edgewise, Notch AISO 1793.5 KJ/m
Charpy Notched Impact Strength23℃, Type 1, Edgewise, Notch AISO 1793.5 KJ/m
Tensile stressBreakISO 527-147 MPa
Tensile strain23℃, 5 mm/min，BreakISO 527-19.7 %
Tensile modulus23 ℃, 1.0 mm/minISO 527-13500 MPa
bending strength23℃ISO 17890 MPa
Suspended wall beam without notch impact strength23 ℃, Type 1ISO 18037 KJ/m
Impact strength of cantilever beam gap23℃, Type 1, Notch AISO 1803.5 KJ/m
Tensile modulusISO 527-23500 Mpa
tensile strengthBreakISO 527-247.0 Mpa
Tensile strainBreakISO 527-210 %
Tensile creep modulus1hrISO 899-13500 Mpa
Tensile creep modulus1000hrISO 899-12400 Mpa
bending strengthISO 17890.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.80 Mpa，UnannealedISO 75A-160 ℃
UL flame retardant rating1.50 mmUL 94HB
UL flame retardant rating3.00 mmUL 94HB
Melting temperatureISO 3146225 ℃
Linear coefficient of thermal expansion平行Flow，23 to 55℃(73 to 130°F)ISO 11359-10.00011 cm/cm/℃
Linear coefficient of thermal expansion垂直Flow，23 to 55℃(73 to 130°F)ISO 11359-10.00011 cm/cm/℃
Hot deformation temperature0.45 Mpa，UnannealedISO 75B-1185 ℃
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B165 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A65.0 °C
Vicat softening temperatureISO 306/B50195 °C
Melting temperatureISO 11357-3225 °C
Linear coefficient of thermal expansionMDISO 11359-21.1E-04 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-21.1E-04 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rate23C/59RHISO 620.35 %
Water absorption rateSat/23CISO 620.2 %
Shrinkage rateAcross FlowISO 294-41.6 %
Shrinkage rateFlowISO 294-41.8 %
densityISO 11831.45
densityISO 11831.45 g/cm³
Shrinkage rateTDISO 294-41.6 %
Shrinkage rateMDISO 294-41.8 %
Water absorption rateSaturation,23°C,2.00mmISO 620.35 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.20 %
MediumDensity1.25 g/cm³
Top out temperature170 °C
SpecificHeatCapacity of Melt1850 J/kg/°C
ThermalConductivityofMelt0.25 W/m/K
Electrical performanceTest ConditionTest MethodTest Result
Dielectric strengthIEC 60243-125 KV/mm
Relative permittivity100HzIEC 602504.00
Relative permittivity1MHzIEC 602503.70
Dissipation factor100HzIEC 602509E-03
Dissipation factor1MHzIEC 602500.016
Compared to the anti leakage trace indexIEC 60112PLC 2
Volume resistivityIEC 60093>1.0E+15 ohms·cm
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.