PBT SO653 NC010 DuPont, European Union
Crastin® 
Electronic and electrical components,Automotive Applications
Low warpage,Filler: Glass beads,20% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Other performanceTest ConditionTest MethodDuPont, European Union/SO653 NC010
Limiting Oxygen IndexISO 4589-122 %
Impact resistanceTest ConditionTest MethodDuPont, European Union/SO653 NC010
Suspended wall beam without notch impact strength-30°CISO 180/1U34 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA3.5 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U37 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA3.5 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A4.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU40 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A3.5 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU50 kJ/m²
Mechanical propertiesTest ConditionTest MethodDuPont, European Union/SO653 NC010
Tensile modulusISO 527-23500 Mpa
bending strength23℃ISO 17890 MPa
Tensile creep modulus1000hISO 899-12400 MPa
1000hrISO 899-12400 Mpa
tensile strength 断裂ISO 527-247.0 Mpa
Charpy Notched Impact Strength23℃, Type 1, Edgewise, Notch AISO 1793.5 KJ/m
Tensile modulus23 ℃, 1.0 mm/minISO 527-13500 MPa
Tensile stress断裂ISO 527-147 MPa
Impact strength of cantilever beam gap23℃, Type 1, Notch AISO 1803.5 KJ/m
Tensile creep modulus1hrISO 899-13500 Mpa
1hISO 899-13500 MPa
bending strengthISO 17890.0 Mpa
Tensile strain断裂ISO 527-210 %
Impact strength of simply supported beam without notch23℃, Type 1, EdgewiseISO 17940 KJ/m
Suspended wall beam without notch impact strength23 ℃, Type 1ISO 18037 KJ/m
Tensile strain23℃, 5 mm/min，断裂ISO 527-19.7 %
Charpy Notched Impact Strength-30℃, Type 1, Edgewise, Notch AISO 1793.5 KJ/m
Electrical performanceTest ConditionTest MethodDuPont, European Union/SO653 NC010
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
dielectric strengthIEC 60243-125 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
relative permittivity100HzIEC 602504.00
Dissipation Factor100HzIEC 602509E-03
relative permittivity1MHzIEC 602503.70
Dissipation Factor1MHzIEC 602500.016
flammabilityTest ConditionTest MethodDuPont, European Union/SO653 NC010
UL flame retardant rating3.0mmIEC 60695-11-10,-20HB
3.0mmUL 94HB
Fogging-G-valuecondensateISO 64521E-04 g
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302SE/B
UL flame retardant rating1.5mmUL 94HB
Limiting Oxygen IndexISO 4589-222 %
burning rate1.00mmISO 379524 mm/min
physical property Test ConditionTest MethodDuPont, European Union/SO653 NC010
Water absorption rateSat/23CISO 620.2 %
Shrinkage rateFlowISO 294-41.8 %
Water absorption rate饱和,23°C,2.00mmISO 620.35 %
densityISO 11831.45 g/cm
ISO 11831.45 g/cm³
SpecificHeatCapacity of Melt1850 J/kg/°C
Water absorption rate平衡,23°C,2.00mm,50%RHISO 620.20 %
Shrinkage rateTDISO 294-41.6 %
MDISO 294-41.8 %
MediumDensity1.25 g/cm³
Ejection Temperature170 °C
Shrinkage rateAcross FlowISO 294-41.6 %
Water absorption rate23C/59RHISO 620.35 %
ThermalConductivityofMelt0.25 W/m/K
Thermal performanceTest ConditionTest MethodDuPont, European Union/SO653 NC010
UL flame retardant rating3.00 mmUL 94HB
Linear coefficient of thermal expansion平行流动方向，23 to 55℃(73 to 130°F)ISO 11359-10.00011 cm/cm/℃
vicatISO 306/B50195 °C
Heat distortion temperature1.80 Mpa，未退火，HDTISO 75A-160 ℃
melting temperatureISO 11357-3225 °C
ISO 3146225 ℃
Heat distortion temperature0.45 Mpa，未退火，HDTISO 75B-1185 ℃
0.45MPa,未退火，HDTISO 75-2/B165 °C
1.8MPa,未退火，HDTISO 75-2/A65.0 °C
Linear coefficient of thermal expansion垂直流动方向，23 to 55℃(73 to 130°F)ISO 11359-10.00011 cm/cm/℃
MDISO 11359-21.1E-04 cm/cm/°C
UL flame retardant rating1.50 mmUL 94HB
Linear coefficient of thermal expansionTDISO 11359-21.1E-04 cm/cm/°C