PA66 Zytel® 70G43L NC010 DUPONT SHENZHEN
386
- Unit Price:US$ 3,506 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:125MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜high strength
- Application Areas:Electrical field｜Electronic field｜Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M -Sale | ISO 2039-2 | 105 |
| R -Sale | ISO 2039-2 | 125 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 262 °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 255 °C | |
| Glass transition temperature | ISO 11357-2 | 80.0 °C | |
| Vicat softening temperature | ISO 306/B50 | 255 °C | |
| Melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 1.5E-5 cm/cm/°C |
| Flow : -40 to 23°C | ISO 11359-2 | 2.0E-5 cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 9.0E-6 cm/cm/°C | |
| Across Flow | ISO 11359-2 | 7.9E-5 cm/cm/°C | |
| Across Flow : -40 to 23°C | ISO 11359-2 | 6.1E-5 cm/cm/°C | |
| Across Flow : 55 to 160°C | ISO 11359-2 | 1.3E-4 cm/cm/°C | |
| Effective thermal diffusivity coefficient | 9.50E-8 m²/s |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning rate | 1.00 mm | ISO 3795 | 27 mm/min |
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 23 % | |
| FMVSS combustion rate | FMVSS 302 | B |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt density | 1.29 g/cm³ | ||
| Top out temperature | 210 °C | ||
| Specific Heat Capacity of Melt | 2050 J/kg/°C | ||
| Thermal Conductivity of Melt | 0.25 W/m/K |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 横向Flow | ISO 294-4 | 1.0 % |
| Flow | ISO 294-4 | 0.30 % | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.90 % |
| Saturation, 23°C, 2.00 mm | ISO 62 | 4.7 % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface resistivity | IEC 62631-3-2 | -- ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| Dielectric strength | IEC 60243-1 | 27 KV/mm | |
| Relative permittivity | 1 MHz | IEC 62631-2-1 | 4.10 |
| 100 Hz | IEC 62631-2-1 | 4.50 | |
| Dissipation factor | 100 Hz | IEC 62631-2-1 | 0.010 |
| 1 MHz | IEC 62631-2-1 | 0.015 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 285 to 305 °C | ||
| Melt Temperature, Optimum | 295 °C | ||
| Mold temperature | 70 to 120 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| Maintain pressure | 50.0 to 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Maximum Screw Tangential Speed | 12 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 14000 Mpa | |
| tensile strength | Break | ISO 527-2 | 225 Mpa |
| Tensile strain | Break | ISO 527-2 | 3.0 % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- Mpa |
| 1000 hr | ISO 899-1 | -- Mpa | |
| Bending modulus | ISO 178 | 12000 Mpa | |
| bending strength | ISO 178 | 340 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 85 kJ/m² |
| 23°C | ISO 179/1eU | 100 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 110 kJ/m² |
| 23°C | ISO 180/1U | 110 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.