PA66
PA66 DUPONT SHENZHEN 70G43L NC010
Injection grade
US$ 3,488 / MT
FOB Shenzhen Port
Physical propertiesTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Water absorption rateSaturation, 23°C, 2.00 mmISO 624.7 %
Equilibrium, 23°C, 2.00 mm, 50% RHISO 621.5 %
Shrinkage rateFlowISO 294-40.30 %
Water absorption rate24 hr, 23°C, 2.00 mmISO 620.90 %
Shrinkage rate横向FlowISO 294-41.0 %
mechanical propertiesTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
bending strengthISO 178340 Mpa
Tensile strainBreakISO 527-23.0 %
Tensile modulusISO 527-214000 Mpa
Bending modulusISO 17812000 Mpa
tensile strengthBreakISO 527-2225 Mpa
Tensile creep modulus1000 hrISO 899-1-- Mpa
1 hrISO 899-1-- Mpa
thermal performanceTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Linear coefficient of thermal expansionAcross FlowISO 11359-27.9E-5 cm/cm/°C
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B262 °C
1.8 MPa, UnannealedISO 75-2/A255 °C
Linear coefficient of thermal expansionFlow : 55 to 160°CISO 11359-29.0E-6 cm/cm/°C
Melting temperatureISO 11357-3262 °C
Vicat softening temperatureISO 306/B50255 °C
Effective thermal diffusivity coefficient9.50E-8 m²/s
Linear coefficient of thermal expansionFlowISO 11359-21.5E-5 cm/cm/°C
Flow : -40 to 23°CISO 11359-22.0E-5 cm/cm/°C
Across Flow : -40 to 23°CISO 11359-26.1E-5 cm/cm/°C
Across Flow : 55 to 160°CISO 11359-21.3E-4 cm/cm/°C
Glass transition temperatureISO 11357-280.0 °C
injectionTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Melt Temperature, Optimum295 °C
Hold Pressure Time3.00 s/mm
Mold temperature70 to 120 °C
Processing (melt) temperature285 to 305 °C
Maximum Screw Tangential Speed12 m/min
Maintain pressure50.0 to 100 Mpa
Drying time - hot air dryer2.0 to 4.0 hr
Suggested maximum moisture content0.20 %
drying temperature80 °C
Mold Temperature, Optimum100 °C
Maintain pressureDrying Recommendedyes
flammabilityTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
FMVSS combustion rateFMVSS 302B
Extreme Oxygen IndexISO 4589-223 %
UL flame retardant ratingUL 94HB
Burning rate1.00 mmISO 379527 mm/min
Electrical performanceTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Dissipation factor100 HzIEC 62631-2-10.010
Volume resistivityIEC 62631-3-1> 1.0E+13 ohms·m
Surface resistivityIEC 62631-3-2-- ohms
Dielectric strengthIEC 60243-127 KV/mm
Dissipation factor1 MHzIEC 62631-2-10.015
Relative permittivity100 HzIEC 62631-2-14.50
1 MHzIEC 62631-2-14.10
impact performanceTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Impact strength of simply supported beam without notch-30°CISO 179/1eU85 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U110 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU100 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U110 kJ/m²
Filling analysisTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Top out temperature210 °C
Melt density1.29 g/cm³
Thermal Conductivity of Melt0.25 W/m/K
Specific Heat Capacity of Melt2050 J/kg/°C
hardnessTest ConditionTest MethodDUPONT SHENZHEN/70G43L NC010
Rockwell hardnessM -SaleISO 2039-2105
R -SaleISO 2039-2125