Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.5 % |
| Shrinkage rate | | ISO 294-4 | 1.2 % |
| Water absorption rate | | ISO 62 | 1.1 % |
| Water absorption rate | | ISO 62 | 0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 7619-1 | 61 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | UL 94 | HB |
| Flammability level | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 414 Mpa |
| tensile strength | | ISO 527-2 | 23.0 Mpa |
| tensile strength | | ISO 527-2 | 54.0 Mpa |
| tensile strength | | ISO 527-2 | 22.0 Mpa |
| tensile strength | | ISO 527-2 | 21.0 Mpa |
| Tensile strain | | ISO 527-2 | 22 % |
| Tensile strain | | ISO 527-2 | > 300 % |
| Nominal tensile fracture strain | | ISO 527-2 | > 50 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Melt density | | | 0.830 g/cm³ |
| Thermal conductivity of melt | | | 0.20 W/m/K |
| Specific Heat Capacity of Melt | | | 2700 J/kg/°C |
| squeeze out | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 70 to 80 °C |
| drying time | | | 5.0 to 7.0 hr |
| Melt Temperature | | | 220 to 250 °C |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ISO 34-1 | 150 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 70 to 80 °C |
| drying time | | | 5.0 to 7.0 hr |
| Processing (melt) temperature | | | 230 to 290 °C |
| Temperature | | | 25 to 60 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 99.0 °C |
| vicat | | ISO 306/B50 | 164 °C |
| melting temperature | | ISO 11357-3 | 172 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.6E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.