PA12 7033 SP 01 ARKEMA USA
Pebax®
Medical Supplies
High temperature resistan、Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| hardness | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| Supporting hardness | 邵氏 D, 15 秒 | ISO 7619-1 | 61 |
| Mechanical properties | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 414 Mpa | |
| Tensile stress | 10% 应变 | ISO 527-2 | 22.0 Mpa |
| Nominal tensile fracture strain | ISO 527-2 | > 50 % | |
| Tensile stress | 断裂 | ISO 527-2 | 54.0 Mpa |
| 屈服 | ISO 527-2 | 23.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | > 300 % |
| 屈服 | ISO 527-2 | 22 % | |
| Tensile stress | 100% 应变 | ISO 527-2 | 21.0 Mpa |
| Electrical performance | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| CTI | IEC 60112 | -- V | |
| Surface Resistivity | IEC 60093 | -- ohms |
| flammability | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| Flammability level | 3.1 mm | IEC 60695-11-10, -20 | HB |
| 1.6 mm | IEC 60695-11-10, -20 | HB |
| Filling analysis | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| Melt density | 0.830 g/cm³ | ||
| Specific Heat Capacity of Melt | 2700 J/kg/°C | ||
| Thermal conductivity of melt | 0.20 W/m/K |
| squeeze out | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| drying temperature | 70 到 80 °C | ||
| drying time | 5.0 到 7.0 hr | ||
| Melt Temperature | 220 到 250 °C |
| physical property | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.70 % |
| Shrinkage rate | 流量 | ISO 294-4 | 1.2 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 1.1 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.5 % |
| elastomer | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| tear strength | ISO 34-1 | 150 kN/m |
| Thermal performance | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| ISO 11359-2 | 1.6E-4 cm/cm/°C | ||
| Heat distortion temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 99.0 °C |
| Melting temperature 2 | ISO 11357-3 | 172 °C | |
| vicat | ISO 306/B50 | 164 °C |
| injection | Test Condition | Test Method | ARKEMA USA/7033 SP 01 |
|---|---|---|---|
| Temperature | 25 到 60 °C | ||
| Processing (melt) temperature | 230 到 290 °C | ||
| drying temperature | 70 到 80 °C | ||
| drying time | 5.0 到 7.0 hr |