ABS 3325MT TRINSEO NETHERLANDS
229
- Unit Price:US$ 2,748 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:17MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 96.1 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 82.8 °C | |
| 1.8MPa,退火 | ISO 75-2/A | 101 °C | |
| vicat | ASTM D1525 | 108 °C | |
| ISO 306/B50 | 102 °C | ||
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9.4E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 2.00mm | ISO 3795 | 60 mm/min |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| carbon emission | VDA277 | 20.0 µg/g | |
| atomization | 100°C | ISO 6452 | 98 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 310 J/m |
| InstrumentedDartImpact | -29°C,3.20mm,PeakEnergy | ASTM D3763 | 31.7 J |
| -29°C,3.20mm,TotalEnergy | ASTM D3763 | 34.3 J | |
| 23°C,3.20mm,PeakEnergy | ASTM D3763 | 31.1 J | |
| 23°C,3.20mm,TotalEnergy | ASTM D3763 | 45.4 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Apparent density | ISO 60 | 0.65 g/cm³ | |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 2.5 g/10min |
| 220°C/10.0kg | ISO 1133 | 10 g/10min | |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 11.0 cm3/10min |
| shrinkage rate | MD | ASTM D955 | 0.40-0.70 % |
| ISO 294-4 | 0.40-0.70 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 3.3 % |
| elongation | 断裂 | ASTM D638 | 25 % |
| flexural modulus | ASTM D790 | 2210 Mpa | |
| 3.20mm,InjectionMolded | ISO 178 | 2100 Mpa | |
| bending strength | ASTM D790 | 64.5 Mpa | |
| 3.20mm,InjectionMolded | ISO 178 | 65.0 Mpa | |
| Tensile modulus | ASTM D638 | 2070 Mpa | |
| 3.20mm,注塑 | ISO 527-2 | 2200 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 42.3 Mpa |
| Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 43.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.