Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 3325MT TRINSEO NETHERLANDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TRINSEO NETHERLANDS/3325MT |
|---|---|---|---|
| InstrumentedDartImpact | -29°C,3.20mm,PeakEnergy | ASTM D3763 | 31.7 J |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 310 J/m |
| InstrumentedDartImpact | -29°C,3.20mm,TotalEnergy | ASTM D3763 | 34.3 J |
| 23°C,3.20mm,TotalEnergy | ASTM D3763 | 45.4 J | |
| 23°C,3.20mm,PeakEnergy | ASTM D3763 | 31.1 J |
| Mechanical properties | Test Condition | Test Method | TRINSEO NETHERLANDS/3325MT |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2070 Mpa | |
| elongation | 断裂 | ASTM D638 | 25 % |
| Tensile modulus | 3.20mm,注塑 | ISO 527-2 | 2200 Mpa |
| Flexural modulus | 3.20mm,InjectionMolded | ISO 178 | 2100 Mpa |
| bending strength | 3.20mm,InjectionMolded | ISO 178 | 65.0 Mpa |
| ASTM D790 | 64.5 Mpa | ||
| tensile strength | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 43.0 Mpa |
| Tensile strain | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 3.3 % |
| tensile strength | 屈服 | ASTM D638 | 42.3 Mpa |
| Flexural modulus | ASTM D790 | 2210 Mpa |
| flammability | Test Condition | Test Method | TRINSEO NETHERLANDS/3325MT |
|---|---|---|---|
| atomization | 100°C | ISO 6452 | 98 % |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| burning rate | 2.00mm | ISO 3795 | 60 mm/min |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| carbon emission | VDA277 | 20.0 µg/g |
| physical property | Test Condition | Test Method | TRINSEO NETHERLANDS/3325MT |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.70 % |
| Apparent density | ISO 60 | 0.65 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 2.5 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 11.0 cm3/10min |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | TRINSEO NETHERLANDS/3325MT |
|---|---|---|---|
| vicat | ASTM D1525 | 108 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 101 °C |
| vicat | ISO 306/B50 | 102 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 96.1 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9.4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 82.8 °C |