PPO

PPO NORYL™ NH7010 BK1005 SABIC INNOVATIVE SHANGHAI

239

Unit Price:US$ 4,167 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜Chemical resistance｜High rigidity
Application Areas:Electrical applications｜electrical equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	38.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.0 mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	--5	ISO 178	2520 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2470 Mpa
elongation	Break	ISO 527-2/50	8.4 %
	elongation	Break3	ASTM D638	41 %
		elongation	Yield	ISO 527-2/50	4.9 %
		elongation	elongation	Yield3	ASTM D638	5.2 %
tensile strength	Break	ISO 527-2/50	63.0 Mpa
	tensile strength	Break3	ASTM D638	49.0 Mpa
		tensile strength	Yield	ISO 527-2/50	69.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	68.0 Mpa
Tensile modulus	--	ISO 527-2/1	2500 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2250 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	102 Mpa
bending strength	bending strength	--5,6	ISO 178	109 Mpa

injection	Test Condition	Test Method	Test Result
Processing (melt) temperature			300 to 325 °C
Mold temperature			80 to 110 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			20 to 100 rpm
drying temperature			110 to 120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			265 to 315 °C
Temperature in the middle of the barrel			275 to 320 °C
Temperature at the front of the material cylinder			290 to 325 °C
Spray nozzle temperature			300 to 325 °C

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B120	162 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	8.2E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	161 °C
Vicat softening temperature	Vicat softening temperature	--	ASTM D15259	160 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	139 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	139 °C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	8.2E-5 cm/cm/°C
RTI Elec		UL 746	105 °C
RTI Imp		UL 746	105 °C
RTI		UL 746	105 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.050 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.25 %
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.80 %
Melt Volume Flow Rate (MVR)	300°C/5.0 kg	ISO 1133	10.0 cm3/10min
melt mass-flow rate	300°C/5.0 kg	ASTM D1238	10 g/10 min

Electrical performance	Test Method	Test Result
Arc resistance	ASTM D495	PLC 6
Compared to the anti leakage trace index	UL 746	PLC 3
High voltage arc tracing rate	UL 746	PLC 4
Hot wire ignition	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ NH7010 BK1005 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet