Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO NH7010 BK1005 SABIC INNOVATIVE SHANGHAI
NORYL™
Electrical applications、electrical equipment
High mobility、Chemical resistance、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/NH7010 BK1005 |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 38.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/NH7010 BK1005 |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2250 Mpa |
| tensile strength | 屈服3 | ASTM D638 | 68.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 41 % |
| 断裂 | ISO 527-2/50 | 8.4 % | |
| Flexural modulus | --5 | ISO 178 | 2520 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 102 Mpa |
| --5,6 | ISO 178 | 109 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2470 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 63.0 Mpa |
| 屈服 | ISO 527-2/50 | 69.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 4.9 % |
| 屈服3 | ASTM D638 | 5.2 % | |
| tensile strength | 断裂3 | ASTM D638 | 49.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2500 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/NH7010 BK1005 |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| arc resistance | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/NH7010 BK1005 |
|---|---|---|---|
| UL flame retardant rating | 2.0 mm | UL 94 | 5VA |
| 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/NH7010 BK1005 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.050 % |
| melt mass-flow rate | 300°C/5.0 kg | ASTM D1238 | 10 g/10 min |
| Melt volume flow rate | 300°C/5.0 kg | ISO 1133 | 10.0 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.25 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/NH7010 BK1005 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 8.2E-5 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 162 °C |
| -- | ASTM D15259 | 160 °C | |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 8.2E-5 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 161 °C |
| RTI Imp | UL 746 | 105 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Af | 139 °C |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 8.2E-5 cm/cm/°C |
| RTI | UL 746 | 105 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 139 °C |
| RTI Elec | UL 746 | 105 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/NH7010 BK1005 |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 275 to 320 °C | ||
| Temperature at the rear of the barrel | 265 to 315 °C | ||
| Processing (melt) temperature | 300 to 325 °C | ||
| drying temperature | 110 to 120 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the front of the material cylinder | 290 to 325 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 80 to 110 °C | ||
| Spray nozzle temperature | 300 to 325 °C |