POM

POM KOCETAL® K700 KOLON KOREA

365

Unit Price:US$ 2,044 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
28MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:Thin walled components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.5 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	55 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178	2900 Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	2700 Mpa
Tensile strain	Break,23°C	ISO 527-2	25 %
elongation	Break,23°C	ASTM D638	45 %
tensile strength	Yield,23°C	ISO 527-2	65.0 Mpa
tensile strength	tensile strength	23°C	ASTM D638	65.0 Mpa
bending strength	23°C	ASTM D790	97.0 Mpa
bending strength	bending strength	23°C	ISO 178	90.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D1525	162 °C
Linear coefficient of thermal expansion	MD	ASTM D696	1.3E-04 cm/cm/°C
Melting temperature		ASTM D1525	166 °C
Melting temperature	Melting temperature		ISO 11357-3	166 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	158 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	110 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	100 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,60%RH	ASTM D570	0.22 %
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.56 %
Shrinkage rate	MD	ISO 294-4	2.0 %
	Shrinkage rate	TD	ISO 294-4	2.0 %
	Shrinkage rate	Shrinkage rate	MD	ASTM D955	2.0 %
melt mass-flow rate	190°C/2.16kg	ISO 1133	27 g/10min
melt mass-flow rate	melt mass-flow rate	190°C/2.16kg	ASTM D1238	27 g/10min
density		ISO 1183	1.41 g/cm³
density	density		ASTM D792	1.41 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant		ASTM D150	3.70
Dielectric strength		IEC 60243-1	19 KV/mm
Dielectric strength	Dielectric strength		ASTM D149	19 KV/mm
Volume resistivity		IEC 60093	1E+14 ohms·cm
Volume resistivity	Volume resistivity		ASTM D257	1E+14 ohms·cm
Surface resistivity		IEC 60093	1E+16 ohms
Surface resistivity	Surface resistivity		ASTM D257	1E+16 ohms
Dissipation factor	1MHz	ASTM D150	6E-03

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	80
Rockwell hardness	Rockwell hardness	M-Scale	ISO 2039-2	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.