POM K700 KOLON KOREA
KOCETAL®
Thin walled components
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | KOLON KOREA/K700 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 55 J/m |
| hardness | Test Condition | Test Method | KOLON KOREA/K700 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 80 |
| M级 | ISO 2039-2 | 95 |
| Electrical performance | Test Condition | Test Method | KOLON KOREA/K700 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 6E-03 |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| dielectric constant | ASTM D150 | 3.70 |
| Mechanical properties | Test Condition | Test Method | KOLON KOREA/K700 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 25 % |
| bending strength | 23°C | ISO 178 | 90.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 65.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2900 Mpa |
| bending strength | 23°C | ASTM D790 | 97.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2700 Mpa |
| tensile strength | 23°C | ASTM D638 | 65.0 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 45 % |
| flammability | Test Condition | Test Method | KOLON KOREA/K700 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | KOLON KOREA/K700 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 2.0 % |
| TD | ISO 294-4 | 2.0 % | |
| MD | ISO 294-4 | 2.0 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.56 % |
| 平衡,23°C,60%RH | ASTM D570 | 0.22 % | |
| density | ASTM D792 | 1.41 g/cm³ | |
| ISO 1183 | 1.41 g/cm³ | ||
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 27 g/10min |
| 190°C/2.16kg | ISO 1133 | 27 g/10min |
| Thermal performance | Test Condition | Test Method | KOLON KOREA/K700 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| vicat | ASTM D1525 | 162 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 158 °C |
| melting temperature | ASTM D1525 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.3E-04 cm/cm/°C |